Photocatalytic coating
View Patent ↗De-polluting, self-cleaning coating compositions are disclosed which comprise an organic binder having dispersed therein photocatalytic titanium dioxide particles substantially in anatase form which have an average crystallite size between about 1 nm and about 150 nm and which preferably have photocatalytic activity in the presence of visible light. Advantageously, the coatings of the invention do not require pre-activation to achieve high initial photocatalytic activity against pollutants in the air, such as NO x compounds.
1. A self-cleaning, de-polluting paint capable of removing pollutants from the air indoors in the presence of visible light comprising:
(i) from about 5% to about 10% by weight photocatalytic titanium dioxide having an anatase content of about 100%, said photocatalytic titanium dioxide being characterized by an average crystallite size between about 5 nm and about 10 nm, a surface area greater than 250 m 2 /g, and having photocatalytic activity in the presence of visible light;
(ii) one or more additional pigments, such that the total pigment volume concentration of said paint, inclusive of said photocatalytic titanium dioxide, is between about 70% and 90%; and
(iii) an organic latex binder comprising a styrene acrylic copolymer;
said paint being free of siloxane water-repellents and comprising from 0% to less than about 0. 2% by weight inorganic binder, and
said paint being capable of substantial removal of NO x compounds from the air when irradiated with visible light immediately after a dried coating of said paint is formed on a substrate, in the absence of prior activation with water, wherein said substantial removal comprises a reduction in a total concentration of a fixed amount of NO x by at least about 2.5%.
2. The paint according to claim 1 , wherein said photocatalytic titanium dioxide is free of the rutile crystalline form.
3. The paint according to claim 1 , wherein said photocatalytic titanium dioxide has a surface area greater than about 300 m 2 /g.
4. The paint according to claim 1 , wherein said photocatalytic titanium dioxide comprises from about 7% to about 15% by volume of said paint.
5. The paint according to claim 1 , wherein said photocatalytic titanium dioxide comprises about 10% by volume of said paint.
6. The paint according to claim 1 , wherein said one or more additional pigments include calcium carbonate and non-photocatalytic titanium dioxide.
7. The paint according to claim 1 wherein said one or more additional pigments comprise non-photocatalytic titanium dioxide and calcium carbonate, and wherein the total pigment volume concentration is between about 70 and about 75%.
8. The paint according to claim 1 , wherein said organic latex binder consists essentially of said styrene acrylic copolymer, said paint further comprising one or more ingredients selected from the group consisting of solvent, thickeners, dispersants, coalesccnts, anti-foaming agents, bateriocides, and combinations thereof.
9. The paint according to claim 1 , wherein said substantial removal comprises a reduction in the total concentration of a fixed amount of NO x by at least about 5%.
10. The paint according to claim 1 , wherein said substantial removal comprises a reduction in the total concentration of a fixed amount of NO x by at least about 7.5%.
11. A self-cleaning, de-polluting paint capable of removing pollutants from the air indoors in the presence of visible light comprising:
(i) from about 5% to about 10% by volume photocatalytic titanium dioxide in substantially pure anatase form, such that the content of the rutile crystalline form is less than 1 % by weight, said photocatalytic titanium dioxide being characterized by an average crystallite size between about 5 nm and about 10 nm, a surface area greater than 250 m 2 /g, and having photocatalytic activity in the presence of visible light;
(ii) one or more additional pigments, such that the total pigment volume concentration of said paint, inclusive of said photocatalytic titanium dioxide, is between about 70% and about 90%; and
(iii) an organic latex binder comprising a styrene acrylic copolymer;
said paint being free of inorganic binder and free of siloxane water-repellents, and said paint being capable of substantial removal of NO x compounds from the air when irradiated with visible light immediately after a dried coating of said paint is formed on a substrate, in the absence of prior activation with water, wherein said substantial removal comprises reduction in a total concentration of a fixed amount of NO x by at least about 2.5%.
12. The paint according to claim 11 , wherein said photocatalytic titanium dioxide has a surface area greater than about 300 m 2 /g.
13. The paint according to claim 11 , wherein said photocatalytic titanium dioxide comprises from about 7% to about 15% by volume of said paint.
14. The paint according to claim 11 , wherein said photocatalytic titanium dioxide comprises about 10% by volume of said paint.
15. The paint according to claim 11 , wherein said one or more additional pigments include calcium carbonate and non-photocatalytic titanium dioxide.
16. The paint according to claim 11 wherein said one or more additional pigments comprise non-photocatalytic titanium dioxide and calcium carbonate, and wherein the total pigment volume concentration is between about 70 and about 75%.
17. The paint according to claim 11 , wherein said organic latex binder consists essentially of said styrene acrylic copolymer, said paint further comprising one or more ingredients selected from the group consisting of solvent, thickeners, dispersants, coalescents, anti-foaming agents, bateriocides, and combinations thereof.
18. A substrate having applied thereto a coating system comprising:
(a) a layer of de-polluting paint, said de-polluting paint layer being formed by applying to said substrate a paint composition comprising:
(i) from about 5% to about 10% by weight photocatalytic titanium dioxide in substantially pure anatase form, such that the content of the rutile crystalline form is less than 1% by weight, said photocatalytic titanium dioxide being characterized by an average crystallite size between about 5 nm and about 10 nm, a surface area greater than 250 m 2 /g, and having photocatalytic activity in the presence of visible light;
(ii) one or more additional pigments, such that the total pigment volume concentration of said paint, inclusive of said photocatalytic titanium dioxide, is-between about 70% and about 90%; and
(iii) a styrene acrylic copolymer binder; said paint being free of siloxane water-repellents and comprising from 0% to less than about 0.2% by weight inorganic binder, and
(b) a top-coat disposed on said de-polluting layer of paint, said top-coat being formed by applying to said layer of paint a sol comprising an aqueous colloidal dispersion of photocatalytic ultrafine titanium dioxide in anatase crystalline form having a surface area greater than 250 m 2 /g as measured by 5-point BET,
wherein the coating system immediately upon drying is capable of substantial removal of NO x compounds from the air when irradiated with visible light in the absence of prior activation with water, wherein said substantial removal comprises reduction in a total concentration of a fixed amount of NO x by at least about 2.5%.
19. The substrate according to claim 18 , wherein said paint composition is free of inorganic binders and wherein said photocatalytic titanium dioxide comprises from about 7% to about 15% by volume of said paint composition.
20. The substrate according to claim 18 , wherein said aqueous colloidal dispersion of photocatalytic ultrafine titanium dioxide is peptised with base at a pH of about 11.4 (±1).