Micronized wood preservative formulations comprising copper and zinc
View Patent ↗Use of micronized zinc compounds in wood preservation treatments containing micronized copper compounds significantly increases the efficacy of the treatment with respect to that of the copper compounds alone. Micronized copper compounds used at a retention in the range of from 0.005 to 1 pounds per cubic foot (pcf) expressed as CuO equivalent, and zinc compounds are used at a retention in the range of from 0.005 to 1 pcf expressed as ZnO equivalent, the increase in wood preservation efficacy over similar retentions of copper compounds alone can be seen in as little as 24 months.
1. A composition comprising:
a) a particulate copper or copper compound component;
b) a particulate zinc or zinc compound component;
wherein at least 85 wt % of the particles are in the range of from .001 to 25 microns; and
c) a polymeric dispersant, wherein the weight ratio of elemental copper to elemental zinc is in the range of from 15:1 to 1:15.
2. The composition of claim 1 , wherein the weight ratio of elemental copper to elemental zinc is in the range of from 5:1 to 1:5.
3. The composition of claim 1 , wherein the composition comprises at least one of the following copper compounds: copper hydroxide, cupric and/or cuprous oxide, and copper carbonate.
4. The composition of claim 2 , wherein the composition comprises at least one of the following copper compounds: copper hydroxide, cupric and/or cuprous oxide, and copper carbonate.
5. The composition of claim 1 , wherein between 50 wt % to 90 wt % of the particles have a diameter in the range of from 0.001 to 25 microns.
6. A method of preserving wood comprising the steps of:
a) applying to the wood a composition comprising:
1) a particulate copper or copper compound component; and
2) a particulate zinc or zinc compound component;
wherein at least 85 wt % of the particles are in the range of from 0.001 to 25 microns; and
b) impregnating the wood with said particles such that the particulate copper or copper compound component is present at a wood retention in the range of from 0.005 to 1 pounds per cubic foot (pcf) CuO equivalents, and the particulate zinc or zinc compounds are present at a wood retention in the range of from 0.005 to 1 pounds per cubic foot (pcf) ZnO equivalents.
7. The method of claim 6 , wherein the weight ratio of elemental copper to elemental zinc in the composition is in the range of from 15:1 to 1:15.
8. The method of claim 6 , wherein the weight ratio of elemental copper to elemental zinc in the composition is in the range of from 5:1 to 1:5.
9. The method of claim 6 , wherein the composition comprises at least one of the following copper compounds: copper hydroxide, cupric and/or cuprous oxide, and copper carbonate.
10. The method of claim 8 , wherein the composition comprises at least one of the following copper compounds: copper hydroxide, cupric and/or cuprous oxide, and copper carbonate.
11. The method of claim 6 , wherein between 50 wt % to 90 wt % of the particles in the composition have a diameter in the range of 0.001 to 25 microns.
12. The method of claim 6 , wherein the composition applied to the wood further comprises an azole.
13. The method of claim 12 , wherein the azole is tebuconazole.
14. Wood comprising:
1) a particulate copper or copper compound component; and
2) a particulate zinc or zinc compound component;
wherein at least 85 wt % of the particles are in the range of from 0.001 to 25 microns, such that the particulate copper or copper compound component is present at a wood retention in the range of from 0.005 to 1 pounds per cubic foot (pcf) CuO equivalents, and the particulate zinc or zinc compounds are present at a wood retention in the range of from 0.005 to 1 pounds per cubic food (pcf) ZnO equivalents.
15. Wood of claim 14 , wherein the weight ratio of elemental copper to elemental zinc in the wood is in the range of from 15:1 to 1:15.
16. Wood of claim 14 , wherein the weight ratio of elemental copper to elemental zinc in the wood is in the range of from 5:1 to 1:5.
17. Wood of claim 14 , wherein the particular copper or copper compound component comprises at least one of the following copper compounds: copper hydroxide, cupric and/or cuprous oxide, and copper carbonate.
18. Wood of claim 16 , wherein the particular copper or copper compound component comprises at least one of the following copper compounds: copper hydroxide, cupric and/or cuprous oxide, and copper carbonate.
19. Wood of claim 14 , wherein between 50 wt % to 90 wt % of the particles in the wood have a diameter in the range of from 0.001 to 25 microns.
20. Wood of claim 14 further comprising an azole.
21. Wood of claim 20 , wherein the azole is tebuconazole.