Method for airtightly joining reinforced platinum hollow tube with platinum flange
View Patent ↗The present invention provides a new method for airtightly joining a hollow tube made of a reinforced platinum and a flange made of platinum or a platinum alloy, which prevents decreasing of mechanical strength of the hollow tube made of a reinforced platinum due to its joining with a flange. A method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy, which is a method for airtightly joining the outer periphery of a hollow tube made of a reinforced platinum produced by dispersing metal oxides in platinum or a platinum alloy, with a flange made of platinum or a platinum alloy, the method comprising a step of shrink-fitting a ring made of platinum or a platinum alloy to the outer periphery of the hollow tube, a step of heating the hollow tube to which the ring is shrink-fit at from 1,150 to 1,450° C. for from 1 to 10 hours, and a step of welding the flange made of platinum or a platinum alloy to the outer periphery of the ring.
1. A method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of non-reinforced platinum or a non-reinforced platinum alloy, which is a method for airtightly joining the outer periphery of a hollow tube made of a reinforced platinum produced by dispersing metal oxides in platinum or a platinum alloy, with a flange made of non-reinforced platinum or a non-reinforced platinum alloy, the method comprising
shrink-fitting a ring made of non-reinforced platinum or a non-reinforced platinum alloy to the outer periphery of the hollow tube of reinforced platinum;
heating the hollow tube to which the ring is shrink-fit at from 1,150 to 1,450° C. for from 1 to 10 hours;
welding the flange made of non-reinforced platinum or a non-reinforced platinum alloy to the outer periphery of the ring.
2. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein ends of a joined portion of the hollow tube with the ring shrink-fit to the outer periphery of the hollow tube, are provided with deposit weldings.
3. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 2 , which further comprises vacuum-degassing a portion between the hollow tube and the ring shrink-fit to the outer periphery of the hollow tube.
4. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein the metal oxide is an oxide of a metal of Group III, IV or XIII in the Periodic Table.
5. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein the hollow tube has an outer diameter of from 50 to 800 mm and a length of from 200 to 3,000 mm.
6. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein the inner diameter of the ring is from 0.001 D to 0.004 D smaller than D provided that the outer diameter of the hollow tube is D.
7. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein the wall thickness t of the ring is smaller than the wall thickness of the hollow tube made of a reinforced platinum.
8. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein the wall thickness t of the ring is from 0.3 to 2 mm and the wall thickness of the hollow tube is from 0.4 to 5 mm.
9. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein the width w of the ring is from 15 to 100 mm.
10. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein a rolling treatment is applied to the vicinities of upper end and lower end of the ring before carrying out the heating treatment.
11. The method for airtightly joining a hollow tube made of a reinforced platinum with a flange made of platinum or a platinum alloy according to claim 1 , wherein the wall thickness of the flange is from 0.5 to 8 mm.