View Patent ↗An electromagnetic wave absorption material and a manufacturing method thereof are disclosed. Mix 40% to 70% weight percent liquid resin with 30% to 60% weight percent bamboo charcoal evenly. After cooling, pour the mixture into a mold for curing to produce sheet product. The microwave absorption material of the present invention meets environmental requirements.
1. An electromagnetic wave absorption material comprising a cured product of a sheeted bamboo charcoal mixture, said bamboo charcoal mixture consisting of:
40% to 70% by weight of a curable rubber material; and
30% to 60% by weight of a bamboo charcoal.
2. The electromagnetic wave absorption material as claimed in claim 1 , wherein the curable rubber material is selected from the group consisting of natural rubber, polybutadiene rubber, styrene butadiene rubber, ethylene-propylene rubber, butyl rubber, chlorinated butyl rubber, chloroprene rubber, and silicone rubber.
3. The electromagnetic wave absorption material as claimed in claim 1 , wherein said bamboo charcoal mixture consists of:
45% to 60% by weight of said curable rubber material; and
40% to 55% by weight of said bamboo charcoal.
4. The electromagnetic wave absorption material as claimed in claim 1 having a thickness of from 0.5 mm to 5.0 mm.
5. The electromagnetic wave absorption material as claimed in claim 1 having a thickness of from 1.0 mm to 3.0 mm.
6. A manufacturing method of electromagnetic wave absorption material comprising the steps of:
mixing a curable rubber material with a bamboo charcoal, yielding a bamboo charcoal mixture consisting of: 40%-70% by weight of said curable rubber material; and 30%-60% by weight of said bamboo charcoal;
sheeting the bamboo charcoal mixture; and
curing the sheeted bamboo charcoal mixture.
7. The method as claimed in claim 6 , wherein curing is performed by pressing the sheeted bamboo charcoal mixture.