Integral single crystal/columnar grained component and method of casting the same
View Patent ↗A hybrid cast component ( 10 ) including both a columnar grained region ( 12 ) and a single crystal region ( 14 ) integrally formed and joined along a metallurgical boundary ( 32 ) in a single casting operation without the need for any weld or braze. A gas turbine blade formed as such may include a columnar grained airfoil and a single crystal platform without any necessity for a thermally formed joint at the blade fillet area.
1. A method of casting comprising:
providing a mold defining a component shape comprising a first region and a second region;
providing a chill plate;
providing a columnar grained starter block between the chill plate and the first region;
providing a single crystal starter seed between the chill plate and the second region;
introducing molten metal into the mold; and
controlling solidification of the molten metal within the mold to grow a columnar grained material from the columnar grained starter block into the first region and to grow a single crystal material from the single crystal starter seed into the second region, with the columnar grained material and the single crystal material being integrally joined along a boundary during the solidification step without the necessity for a separate metals joining step.
2. The method of claim 1 , further comprising disposing a grain continuator between the single crystal starter seed and the second region.
3. The method of claim 2 , further comprising:
growing the columnar grained material from a bottom region of the component shape proximate the chill plate toward a top region of the component shape; and
locating an outlet end of the grain continuator at the top region of the component shape to direct growth of the single crystal material to avoid the bottom region of the component shape and into only the top region of the component shape.
4. The method of claim 1 further comprising:
forming the mold so that the first region defines an airfoil shape and the second region defines a platform shape; and
controlling solidification of the molten metal within the mold to grow the columnar grained material to form an airfoil and to grow the single crystal material to form a platform, with the columnar grained airfoil and the single crystal platform being integrally joined along a boundary comprising a fillet region.
5. The method of claim 4 , further comprising:
disposing two grain continuators between respective single crystal starter seeds and opposed sides of the second region; and
controlling solidification of the molten metal within the mold to grow the columnar grained material to form the airfoil and to grow single crystal material from a first of the single crystal starter seeds to form a front side of the platform and to grow single crystal material from a second of the single crystal starter seeds to form a back side of the platform.
6. A casting apparatus comprising:
a chill plate;
a mold extending from the chill plate and comprising a first region proximate the chill plate and a second region remote from the chill plate;
a columnar grained starter block disposed between the chill plate and the first region of the mold;
a single crystal starter seed disposed proximate the chill plate but remote from the columnar grained starter block;
a grain continuator disposed between the single crystal starter seed and the second region of the mold;
whereby when molten metal is introduced into the mold, solidification can be controlled within the mold to grow a columnar grained material from the columnar grained starter block into the first region and to grow a single crystal material from the single crystal starter seed into the second region while bypassing the first region, with the columnar grained material and the single crystal material being integrally joined during the solidification step without the necessity for a separate metals joining step.
7. The casting apparatus of claim 6 , wherein the first region defines an airfoil section of a gas turbine blade and the second region defines a platform region of the blade.