Method of sintering AIN under a methane-containing nitrogen atmosphere
View Patent ↗The present method uses a methane-containing nitrogen gas sintering atmosphere to sinter aluminum nitride (AlN) to a high transmittance. The methane gas replaces the solid carbon charge material used in prior art sintering methods as the source of gaseous carbon. The amount of carbon in the methane-containing nitrogen gas is easily controlled by varying the partial pressure of methane in the nitrogen gas. In addition, the methane flow is stopped prior to the end of the sintering cycle to prevent darkening of the sintered part.
1. A method of sintering an aluminum nitride article, comprising the steps of:
(a) placing the aluminum nitride article in a sintering atmosphere, the sintering atmosphere comprising nitrogen gas containing from about 0.05% to about 1% methane by volume;
(b) subjecting the aluminum nitride article to an increasing temperature;
(c) holding the aluminum nitride article at a sintering temperature for a first dwell period;
(d) changing the sintering atmosphere to nitrogen gas that does not contain methane;
(e) continue holding the aluminum nitride article at the sintering temperature for a second dwell period to form a sintered aluminum nitride article, wherein the second dwell period is from about 25% to about 95% of the sum of the first and second dwell periods; and
(f) cooling the sintered aluminum nitride article.
2. The method of claim 1 wherein the sintered AlN article has a high total transmittance.
3. The method of claim 1 wherein the second dwell period is from about 25% to about 50% of the sum of the first and second dwell periods.
4. The method of claim 1 wherein the increasing temperature increases at a rate of less than about 10° C./minute.
5. The method of claim 4 wherein the increasing temperature increases at a rate of from about 2° C./minute to about 5° C./minute.
6. The method of claim 1 wherein the sintering temperature is from about 1800° C. to about 1950° C.
7. The method of claim 1 wherein the sintering temperature is from about 1900° C. to about 1925° C.
8. The method of claim 1 wherein the sum of the first and second dwell periods is from about 30 minutes to about 40 hours.
9. The method of claim 1 wherein the sum of the first and second dwell periods is from about 10 hours to about 25 hours.
10. A method of sintering an aluminum nitride article, comprising the steps of:
(a) placing the aluminum nitride article in a sintering atmosphere, the sintering atmosphere comprising nitrogen gas containing from about 0.05% to about 1% methane by volume;
(b) subjecting the aluminum nitride article to an increasing temperature that increases at a rate of less than about 10° C./minute;
(c) holding the aluminum nitride article at a sintering temperature for a first dwell period;
(d) changing the sintering atmosphere to nitrogen gas that does not contain methane;
(e) continue holding the aluminum nitride article at the sintering temperature for a second dwell period to form a sintered aluminum nitride article, wherein the sintering temperature is from about 1800° C. to about 1950° C. and the second dwell period is from about 25% to about 95% of the sum of the first and second dwell periods; and
(f) cooling the sintered aluminum nitride article.
11. The method of claim 10 wherein the second dwell period is from about 25% to about 50% of the sum of the first and second dwell periods.
12. The method of claim 10 wherein the sum of the first and second dwell periods is from about 30 minutes to about 40 hours.
13. The method of claim 12 wherein the increasing temperature increases at a rate of from about 2° C./minute to about 5° C./minute.
14. The method of claim 13 wherein the second dwell period is from about 25% to about 50% of the sum of the first and second dwell periods.
15. The method of claim 14 wherein the sintering temperature is from about 1900° C. to about 1925° C.
16. The method of claim 15 wherein the sum of the first and second dwell periods is from about 10 hours to about 25 hours.