Bleaching of pulp
View Patent ↗The present invention relates to a process of bleaching pulp derived from an alkaline pulping process having a hexenuronic acid content prior to the final bleaching stage from about 1 to about 80 mmol/kg dry pulp, said process comprising three chlorine dioxide stages D0, D1, and D2, wherein the chlorine dioxide charges based on the total chlorine dioxide charge in a) D0 is from about 40 to about 60%; b) D1 is from about 30 to about 55%; c) D2 is from about 4 to about 20%, and wherein the final chlorine dioxide stage D2 is performed at a pH from about 2 to about 4.5. The invention also relates to a bleached pulp obtainable by the process.
1. A process of bleaching pulp derived from an alkaline pulping process, said process comprising three chlorine dioxide stages D0, D1, and D2, wherein the chlorine dioxide charges based on the total chlorine dioxide charge in
a) D0 is from 40 to 60%;
b) D1 is from 30 to 55%;
c) D2 is from 4 to 20%, wherein the pulp has a hexenuronic acid content after the D1 stage and prior to the final D2 bleaching stage from about 1 to about 80 mmol/kg dry pulp, wherein the final chlorine dioxide stage D2 is performed at a pH from 2 to 3.5, and wherein said process further comprises an oxygen-containing peroxide stage OP between the D0 and D1 stages.
2. The process according to claim 1 , wherein said process further comprises a neutral washing stage n between the D1 and D2 stages, wherein the pH is adjusted to a value in the range of from 7 to 10 in said n stage.
3. The process according to claim 2 , wherein the chlorine dioxide stage D0 is performed at a retention time of about 20 to about 60 minutes.
4. The process according to claim 3 , wherein the temperature of the D0 stage ranges from 55 to 70° C. and the temperature of the final chlorine dioxide bleaching stage D2 ranges from 85 to 100° C.