Coated sheet, method of formation thereof, and article derived therefrom
View Patent ↗A sheet material includes a polycarbonate substrate and a protective coating containing the reaction products of an aminoplast resin, a polyol compound, and a UV-absorbing amount of a triazine compound. The sheet material exhibits an improved balance of abrasion resistance, solvent resistance, weatherability, and formability. Methods of preparing the sheet material are described.
1. A method of producing a sheet, comprising:
coating a curable composition on a face of a polycarbonate sheet, wherein the curable composition consists of
an aminoplast resin, wherein the aminoplast resin is a melamine-formaldehyde resin having the structure
wherein each occurrence of R 1 is independently hydrogen, a methylene bridge to another melamine nucleus, or CH 2 OR 2 , wherein R 2 is hydrogen or C 1 -C 12 alkyl;
a polyol compound, wherein the polyol compound comprises an oligomeric aliphatic polyestercarbonate diol having a number average molecular weight of at least 200 atomic mass units;
a UV-absorbing amount of a triazine compound, wherein the triazine compound has the structure
wherein each occurrence of Ar is independently phenyl or substituted phenyl; wherein the substituents on the phenyl group may be hydroxy, amino, C 1 -C 12 hydrocarbyl, C 1 -C 12 hydrocarbyloxy, or C 1 -C 12 hydrocarbylamino; and R 7 is hydrogen, C 1 -C 16 hydrocarbyl wherein the hydrocarbyl group may contain nitrogen or oxygen heteroatoms, or
wherein R 8 is hydrogen or C 1 -C 16 hydrocarbyl wherein the hydrocarbyl group may contain nitrogen or oxygen heteroatoms; and
optionally, one or more of
a solvent selected from C 1 -C 12 alcohols, C 3 -C 12 ketones, C 3 -C 12 esters, C 4 -C 12 ethers, C 3 -C 12 alkoxy alkanols, C 1 -C 12 halogenated hydrocarbons, C 2 -C 12 carboxylic acids, C 6 -C 18 aromatic compounds, and mixtures thereof,
a hindered amine light stabilizer,
a curing catalyst selected from alkyl acid phosphates, dialkyl acid phosphates, phosphoric acid, maleic acid, maleic anhydride, fumaric acid, chloromaleic acid, chloromaleic anhydride, alkyl acid phthalates, monoalkyl succinates, monoalkyl maleates, alkyl sulfonic acids, aryl sulfonic acids, sulfamic acid, and mixtures thereof,
a catalyst stabilizer, and
an additive selected from flow control agents, surfactants, viscosity modifiers, antifoaming agents, and mixtures thereof; and
curing the curable composition to form a protective layer having a thickness of about 2 to about 40 micrometers.
2. The method of claim 1 , wherein said coating comprises flow coating.
3. The method of claim 1 , wherein said coating comprises dip coating.
4. The method of claim 1 , wherein the curable composition comprises about 20 to about 80 weight percent of the aminoplast resin, based on the total weight of curable solids.
5. The method of claim 1 , wherein the curable composition comprises about 20 to about 80 weight percent of the polyol, based on the total weight of curable solids.
6. The method of claim 1 , wherein the curable composition comprises about 0.1 to about 10 weight percent of the triazine, based on the total weight of curable solids.
7. The method of claim 1 , wherein the curable composition comprises the solvent.
8. The method of claim 7 , wherein the solvent comprises 1-methoxy-2-propanol, 1-butoxy-2-propanol, or a mixture thereof.
9. The method of claim 1 , wherein the curable composition comprises the curing catalyst.
10. The method of claim 1 , wherein the curable composition comprises the catalyst stabilizer; and wherein the catalyst stabilizer is selected from the group consisting of triethylamine, pyridine, 2-methylaminoethanol, and mixtures thereof.
11. The method of claim 1 wherein the curable composition comprises the hindered amine light stabilizer.