Liquid low-sodium silicate electrolyte used for a storage battery and manufactured by magentization process, and the usage thereof
View Patent ↗A liquid low concentration sodium-containing silicate solution as electrolyte for lead-acid storage batteries and its applications, is prepared by mixing a silica gel containing 40˜60 wt % SiO 2 , the weight units of such a silica gel are 5˜15; add 15-25 weight units water and stir until the concentration of the mixture is 0.65˜0.85 0 Be′ measured by a Baum densimeter, adjusting the pH value of this mixture to 1-4 using inorganic acid and magnetizing the mixture under 1000-6000 Gauss magnetic field for 5-10 minutes, stir the magnetized mixture until the viscosity of the mixture is less than 0.02 poise and finally obtain a liquid low concentration sodium-containing silicate solution. The electrolyte can be used as electrolyte or activation solution for common or special lead-acid storage batteries.
1. A method of making a magnetically treated low concentration sodium-containing silicate solution for a lead-acid storage battery, comprising:
1) preparing 5˜15 weight units of a silica gel containing 40˜60 wt % SiO 2 ;
2) adding 15˜25 weight units of water to the silica gel and stirring the mixture at the same time, until the concentration is 0.65˜0.85 0 Be′ measured using a Baume′ densimeter;
3) adding inorganic acid to the solution of step 2) until a pH value is 1-4 to obtain a silicate mixture;
4) exposing the silicate mixture obtained in step 3) to a magnetic field of 1000-6000 Gauss for 5-10 minutes to obtain a magnetized mixture; and
5) stirring the magnetized mixture obtained in step 4) until the viscosity of the magnetized mixture is less than 0.02 poise.
2. A method as set forth in claim 1 , wherein the water is deionized water or distilled water.
3. A method as set forth in claim 1 , wherein the inorganic acid is one of hydrochloric acid, oxalic acid, sulfuric acid.
4. A method as set forth in claim 1 , wherein the stirring speed is 700˜1400 r/m, and wherein the stirring is continued for 5˜10 minutes.
5. A method as set forth in claim 1 , wherein the magnetic field is generated using a round tube of NdFeB with a 1000-6000 Gauss magnetic intensity.