Electrochemical device comprising alkaline electroylte
View Patent ↗An electrochemical device, such as an alkaline battery, that is excellent in leakage-resistance and storage characteristics is provided by controlling at least one of the following two conditions with respect to at least the inner side surface of a battery case comprising a nickel plated steel plate. The two conditions are: (1) the intensity ratio of Fe to Ni (I Fe/Ni ) as determined by electron probe microanalysis; and (2) the ratio of the area with an intensity ratio of Fe to Ni (I Fe/Ni ) of greater than 1.0 as determined by electron probe microanalysis to the whole area.
1. An electrochemical device comprising:
a positive electrode comprising a positive electrode active material selected from the group consisting of nickel oxyhydroxide, manganese dioxide, and a mixture of nickel oxyhydroxide and manganese dioxide;
a negative electrode comprising a zinc component as a negative electrode active material;
a separator interposed between said positive electrode and said negative electrode;
an alkaline electrolyte; and
a battery case, formed into a battery can shape, for housing said positive electrode, said negative electrode, said separator, and said alkaline electrolyte, wherein:
said battery case includes a nickel plated steel plate having a nickel plating layer at least on an inner side surface of the battery case, and
at least the inner side surface of the battery case has a surface structure satisfying that an intensity ratio of Fe to Ni (I Fe/Ni ) as determined by electron probe microanalysis is from approximately 0.002 to approximately 0.005.
2. The electrochemical device in accordance with claim 1 , wherein said inner side surface of said battery case further has a conductive layer.
3. The electrochemical device in accordance with claim 1 , wherein:
said positive electrode active material includes manganese dioxide, and
said manganese dioxide in said positive electrode contains approximately 2000 to approximately 7000 ppm of residual Na.
4. The electrochemical device in accordance with claim 1 , wherein:
said positive electrode active material includes manganese dioxide, and
said manganese dioxide in said positive electrode contains approximately 2000 to approximately 5000 ppm of residual Na.
5. The electrochemical device in accordance with claim 1 , wherein said alkaline electrolyte is an aqueous solution containing more than or equal to approximately 32% by weight of potassium hydroxide.
6. The electrochemical device in accordance with claim 1 , wherein said nickel plating layer has a thickness of approximately 0.2 to approximately 1.0 μm.
7. An electrochemical device comprising:
a positive electrode comprising a positive electrode active material selected from the group consisting of nickel oxyhydroxide, manganese dioxide, and mixtures of nickel oxyhydroxide and manganese dioxide;
a negative electrode comprising a zinc component as a negative electrode active material;
a separator interposed between said positive electrode and said negative electrode;
an alkaline electrolyte; and
a battery case, formed into a battery can shape, for housing said positive electrode, said negative electrode, said separator, and said alkaline electrolyte, wherein:
said battery case includes a nickel plated steel plate having a nickel plating layer at least on an inner side surface of the battery case, and
at least the inner side surface of the battery case has a surface structure satisfying that a ratio of an area with an intensity ratio of Fe to Ni (I Fe/Ni ) of greater than 1.0 as determined by electron probe microanalysis to a whole area is approximately 1.0% or less.
8. The electrochemical device in accordance with claim 7 , wherein said inner side surface of said battery case further has a conductive layer.
9. The electrochemical device in accordance with claim 7 , wherein said ratio of an area with an intensity ratio of Fe to Ni (I Fe/Ni ) of greater than 1.0 is approximately 0.01 to approximately 0.7%.
10. The electrochemical device in accordance with claim 7 , wherein said ratio of an area with an intensity ratio of Fe to Ni (I Fe/Ni ) of greater than 1.0 is approximately 0.01 to approximately 0.3%.
11. The electrochemical device in accordance with claim 7 , wherein:
said positive electrode active material includes manganese dioxide, and
said manganese dioxide in said positive electrode contains approximately 2000 to approximately 7000 ppm of residual Na.
12. The electrochemical device in accordance with claim 7 , wherein:
said positive electrode active material includes manganese dioxide, and
said manganese dioxide in said positive electrode contains approximately 2000 to approximately 5000 ppm of residual Na.
13. The electrochemical device in accordance with claim 7 , wherein said alkaline electrolyte is an aqueous solution containing more than or equal to approximately 32% by weight of potassium hydroxide.
14. The electrochemical device in accordance with claim 7 , wherein said nickel plating layer has a thickness of approximately 0.2 to approximately 1.0 μm.
15. An electrochemical device comprising:
a positive electrode comprising a positive electrode active material selected from the group consisting of nickel oxyhydroxide, manganese dioxide, and mixtures of nickel oxyhydroxide and manganese dioxide;
a negative electrode comprising a zinc component as a negative electrode active material; a separator interposed between said positive electrode and said negative electrode;
an alkaline electrolyte; and
a battery case, formed into a battery can shape, for housing said positive electrode, said negative electrode, said separator, and said alkaline electrolyte, wherein:
said battery case includes a nickel plated steel plate having a nickel plating layer at least on an inner side surface of the battery case, and
at least the inner side surface of the battery case has a surface structure satisfying that an intensity ratio of Fe to Ni (I Fe/Ni ) as determined by electron probe microanalysis is from approximately 0.002 to approximately 0.005 and a ratio of an area with an intensity ratio of Fe to Ni (I Fe/Ni ) of greater than 1.0 as determined by electron probe microanalysis to a whole area is approximately 1.0% or less.
16. The electrochemical device in accordance with claim 15 , wherein said inner side surface of said battery case further has a conductive layer.
17. The electrochemical device in accordance with claim 15 , wherein said ratio of an area with an intensity ratio of Fe to Ni (I Fe/Ni ) of greater than 1.0 is approximately 0.01 to approximately 0.7%.
18. The electrochemical device in accordance with claim 15 , wherein said ratio of an area with an intensity ratio of Fe to Ni (I Fe/Ni ) of greater than 1.0 is approximately 0.01 to approximately 0.3%.
19. The electrochemical device in accordance with claim 15 , wherein:
said positive electrode active material includes manganese dioxide, and
said manganese dioxide in said positive electrode contains approximately 2000 to approximately 7000 ppm of residual Na.
20. The electrochemical device in accordance with claim 15 , wherein:
said positive electrode active material includes manganese dioxide, and
said manganese dioxide in said positive electrode contains approximately 2000 to approximately 5000 ppm of residual Na.
21. The electrochemical device in accordance with claim 15 , wherein said alkaline electrolyte is an aqueous solution containing more than or equal to approximately 32% by weight of potassium hydroxide.
22. The electrochemical device in accordance with claim 15 , wherein said nickel plating layer has a thickness of approximately 0.2 to approximately 1.0 μm.