Slag concrete manufactured aggregate
View Patent ↗Embodiments of the invention provide a slag manufactured aggregate suitable for inclusion in one or more of concrete, precast concrete, cellular concrete, or precast cellular concrete. Concretes, precast concretes, cellular concretes, and precast cellular concretes comprising the slag manufactured aggregate are also included in embodiments of the invention. Methods of making the foregoing aggregates and concretes are also included herein.
1. A slag concrete manufactured aggregate comprising:
5% to 50% cement by weight, 50% to 94% demetallized stainless steel slag by weight, 0% to 90% foaming agent by volume, 2 to 20 ounces per hundredweight of cement of at least one admixture, 0% to 10% of a natural, synthetic or steel fiber by weight, and 0% to 10% coloring agents by weight.
2. The slag concrete manufactured aggregate of claim 1 , wherein between 5% and 95% by weight of said cement is replaced by at least one pozzolanic material selected from the group consisting of silica fume, metakaolin, fly ash, rice hull ash, silica flour, cement kiln dust, and ground granulated blast furnace slag.
3. The slag concrete manufactured aggregate of claim 2 , wherein said at least one pozzolanic material is present in an amount of 5 to 95% by weight ground granulated blast furnace slag, 5% to 90% by weight flyash, 10% to 75% by weight cement kiln dust, 0.5% to 25% by weight silica fume, 0.5% to 25% by weight metakaolin, and 5% to 90% by weight rice hull ash.
4. The slag concrete manufactured aggregate of claim 1 , wherein said slag concrete manufactured aggregate does not include ground granulated blast furnace slag.
5. The slag concrete manufactured aggregate of claim 1 wherein said demetallized stainless steel slag has a metal content less than 5% by weight.
6. The slag concrete manufactured aggregate of claim 1 , wherein said demetallized stainless steel slag has an average particle size of less than 1 inch.
7. The slag concrete manufactured aggregate of claim 1 , wherein said at least one admixture is selected from one or more members of the group consisting of plasticizers, superplasticizers, water reducers, retarders, air entraining agents, accelerators, foaming agents, water repellents, and consolidating concrete chemicals.
8. The slag concrete manufactured aggregate of claim 1 , comprising 0.5% to 10% by weight of a natural, synthetic, or steel fiber.
9. The slag concrete manufactured aggregate of claim 5 wherein said demetallized stainless steel slag has a metal content less than 1% by weight.