View Patent ↗Molding material that includes a layer of fibrous reinforcing material having one surface on which a first layer of a resin partially impregnates the fibrous material and a further resin layer located on the opposite surface which retains in position surface fibers of the fibrous material. The further resin layer is of lower weight than the first layer and is formed as an openwork structure with a solid part and spaces through which the fibrous material is exposed.
1. A method of forming a moulding material for use in making a moulded product, said method comprising the steps of:
providing a layer of fibrous reinforcing material having a first side and a second side and wherein the fibrous reinforcing material consists essentially of fibers extending in a common direction;
applying a first layer of resin to said first side of said fibrous reinforcing material such that said first layer of resin partially impregnates the fibrous reinforcing material on said first side, said first layer of resin providing a solid film without openings therein and wherein said resin of said first layer amounts to 30 to 50% by weight of said moulding material; and
applying a further layer of resin to said second side of said fibrous reinforcing material to form said moulding material, said further layer of resin forming an openwork structure with a solid part and spaces through which the fibrous reinforcing material is exposed and wherein said resin of said further layer amounts to 0.1 to 20% by weight of said moulding material, wherein said first layer of resin and said further layers of resin together amount to 30.1 to 70% by weight of said moulding material.
2. A method of forming a moulding material according to claim 1 wherein the fibrous reinforcing material comprises multiple side-by-side fiber tows.
3. A method of forming a moulding material according to claim 1 wherein said moulding material is in the form of an elongated structure wherein said common direction extends longitudinally relative to said structure.
4. A method of forming a moulding material according to claim 1 wherein the fibrous reinforcing material comprises carbon fiber material.
5. A method of forming a moulding material according to claim 1 wherein the fibrous reinforcing material comprises discontinuous fibers.
6. A method of forming a moulding material according to claim 1 wherein said first layer of resin comprises a heat-curable thermosetting resin matrix.
7. A method of forming a moulding material according to claim 1 wherein said first layer of resin and said further layer of resin are formed from the same resin.
8. A method of forming a moulding material according to claim 1 wherein the solid part of said further layer of resin occupies a minor proportion of the surface area of the fibrous layer, said spaces therein collectively making up the major part.
9. A method of forming a moulding material according to claim 8 wherein the solid part occupies less than 25% of the surface area.
10. A method of forming a moulding material according to claim 9 wherein the solid part occupies from 4% to 24% of the surface area.
11. A method of forming a moulding material according to claim 1 wherein the solid part comprises a grid pattern of solid linear elements enclosing said spaces.
12. A method of forming a moulding material according to claim 11 wherein said grid pattern is a regular pattern of repeating geometrical shapes.
13. A method of forming a moulding material according to claim 1 wherein said further resin layer comprises a perforate web comprising perforations therein that form said spaces.
14. A method according to claim 1 which includes the additional step of applying a further structure comprising fibrous material to said first layer of resin.
15. A method according to claim 1 which includes the additional step of curing said first and further layers of resin.
16. A method of forming a moulding material according to claim 1 wherein said first resin layer comprises a pre-preg layer.