Anionic copolymers prepared in an inverse emulsion matrix
View Patent ↗A papermaking method and a composition which utilize, as a drainage aid, a water-soluble anionic copolymer prepared via a water-in-oil polymerization technique that, absent a cross-linking agent, is characterized by a Huggins' constant (k′) determined in 0.01M NaCl greater than 0.75 and a storage modulus (G′) for a 1.5 wt. % actives polymer solution at 4.6 Hz greater than 175 Pa.
1. A method of preparing a polymer by water-in-oil emulsion polymerization comprising:
(a) preparing an oil phase comprising: at least one hydrocarbon; and a surfactant system wherein the surfactant system comprises at least one diblock or triblock surfactant to form an emulsion upon the addition of an aqueous phase;
(b) preparing an aqueous phase comprising at least one ethylenically unsaturated anionic monomer and at least one ethylenically unsaturated anionic monomer and at least one ethylenically unsaturated nonionic monomer;
(c) adding said aqueous phase (b) to said oil phase (c) to form an emulsion; and
(d) causing the monomers in the emulsion to polymerize by free radical polymerization;
wherein the diblock or triblock surfactant to monomer ratio is at least about 0.03 and the pH is adjusted to from about 2 to about 7 and wherein no additional crossing linking agent is added to the system, wherein the resulting polymer having a Huggins' constant (k′) determined between 0.0025 wt. % to 0.025 wt. % of said polymer in 0.01 m NaCl is greater than 0.75; and having a storage modulus (G′) for a 1.5 wt. % actives of said polymer solution at 4.6 Hz is greater tan 175 Pa.
2. The method of claim 1 wherein the surfactant system has a combined Hydrophilic-Lipophilic Balance of less than 8.
3. The method of claim 1 wherein the pH is from about 3 to about 6.
4. The method of claim 1 wherein the diblock or triblock surfactant is a copolymer based on polyester derivatives of fatty acids and poly[ethyleneoxide].
5. The method of claim 1 wherein the ethylenically unsaturated nonionic monomer is selected from the group consisting of acrylamide, methacrylamide; N-alkylacrylamides, N,N-dialkyl-acrylamide; methyl formamide; vinyl acetate; N-vinyl pyrrolidone; and mixtures of any of the foregoing.
6. The method of claim 1 wherein the ethylenically unsaturated anionic monomer is selected from the group consisting of the free acids and salts of acrylic acid; methacrylic acid; maleic acid; itaconic acid; acrylamideoglycolic acid; 2-acrylamido-2-methyl-1propanesulfonic acid; 3-allyloxy-2-hydroxy-1-propanesulfonic acid; styrenesulfonic acid; vinylsulfonic acid; vinylphosphonic acid; 2-acrylamido-2-methylpropane phosphonic acid; and mixtures of any of the foregoing.
7. The method of claim 1 wherein the method further comprises adding a free radical initiator.
8. The method of claim 7 wherein the free radical initiator is 2,2′-azobisisobutyronitrile.
9. The method of claim 7 wherein the free radical initiator is lauryl peroxide.
10. The method of claim 7 wherein the free radical initiator is selected from the group consisting of 2,2′-azobis-(2,4-dimethylpentanonitrile), 2,2′-azobis-(2,-methylbutanonitrile, 1,1′-azobis-(cyclohexanecarbonitrile), benzoylperoxide and mixtures of any of the foregoing.
11. The method of claim 1 wherein the diblock or triblock surfactant to monomer ratio is at least about 4:100.
12. The method of claim 1 wherein the nonionic polymer segment B is acrylamide and the anionic polymer segment F is selected from the group consisting of the sodium, potassium or ammonium salt of acrylic acid.
13. The method of claim 1 wherein the surfactant system comprises a) a diblock or triblock surfactant derived from the oil-soluble complex monocarboxylic acid and a water soluble component derived from polyalkylene glycol, and b) a sorbitan fatty acid ester; the pH of the aqueous phase is 3 to 6; and 2,2′-azobisisobutyronitrile is employed as the free radical initiator.
14. The method of claim 1 wherein B is acrylamide and F is a salt of acrylic acid, the molar % ratio of acrylic acid: acrylamide is from about 75:25 to 25:75 and wherein the water in oil emulsion is prepared employing an oil soluble free radical initiator; and an emulsification surfactant package with a combined Hydrophilic-Lipophilic Balance of less than 8 consisting of diblock or triblock polymeric surfactants; and wherein the process further comprises adding a breaker surfactant to enhance the inversion of the emulsion when the polymerized solution is added to water.
15. The method of claim 14 wherein the molar ratio of acrylic acid: acrylamide is from 60:40 to 40:60.