Nickel hydroxide powder, nickel oxyhydroxide powder, method for producing these and alkaline dry battery
In order to provide an alkaline dry battery having excellent heavy load discharge characteristics, suppressed polarization at the time of heavy load pulse discharge, and excellent heavy load discharge characteristics after high temperature storage, a nickel oxyhydroxide powder having a tap density of 2.1 to 2.7 g/cm 3 and including non-spherical and sheet-like nickel oxyhydroxide particles is included in a positive electrode active material.
1 . A nickel hydroxide powder having a tap density of approximately 2.1 to 2.5 g/cm 3 and including non-spherical and sheet-like nickel hydroxide particles.
2 . A method for producing a nickel hydroxide powder comprising the steps of:
obtaining a mixture by adding a nickel hydroxide powder including spherical nickel hydroxide particles into an aqueous sodium hydroxide solution;
aging said mixture;
cooling said mixture after aging to obtain a precipitate having a tap density of approximately 2.1 to 2.5 g/cm 3 and including non-spherical and sheet-like nickel hydroxide particles; and
separating, water-washing and drying said precipitate to obtain a nickel hydroxide powder including said nickel hydroxide particles.
3 . A nickel oxyhydroxide powder having a tap density of approximately 2.1 to 2.7 g/cm 3 and including non-spherical and sheet-like nickel oxyhydroxide particles.
4 . A method for producing a nickel oxyhydroxide powder comprising the steps of:
obtaining a mixture by adding a nickel hydroxide powder including spherical nickel hydroxide particles into an aqueous sodium hydroxide solution;
aging said mixture;
cooling said mixture after aging to obtain a precipitate having a tap density of approximately 2.1 to 2.5 g/cm 3 and including non-spherical and sheet-like nickel hydroxide particles;
separating, water-washing and drying said precipitate to obtain a nickel hydroxide powder including said nickel hydroxide particles; and
oxidizing said nickel hydroxide powder to obtain a nickel oxyhydroxide powder having a tap density of approximately 2.1 to 2.7 g/cm 3 and including non-spherical and sheet-like nickel oxyhydroxide particles.
5 . An alkaline dry battery comprising:
a positive electrode including a positive electrode active material containing at least nickel oxyhydroxide and manganese dioxide, and a conductive agent containing graphite;
a negative electrode including a negative electrode active material containing zinc or a zinc alloy;
a separator interposed between said positive electrode and said negative electrode;
a negative electrode current collector disposed in said negative electrode; and
an alkaline electrolyte,
wherein said nickel oxyhydroxide has a tap density of approximately 2.1 to 2.7 g/cm 3 and includes non-spherical and sheet-like nickel oxyhydroxide particles.