Carbon black, method of producing carbon black, and device for implementing the method
View Patent ↗The invention relates to a carbon black having an aggregate size distribution which has a (d 90 -d 10 )/d 50 ratio of less than or equal to 1.1. The carbon blacks are produced by admixing hot air if desired to a gas mixture comprising a carrier gas and a carbon black feedstock, passing the gas mixture into a burner pipe, burning the gas mixture at the burner pipe openings, and drawing the flames under suction, together with the ambient air drawn in freely under suction from the outside, through a cooled, narrowing gap, and carrying out cooling, the cooled, narrowing gap having a height (h) to width (b) ratio of 1-100, the width (b) being 0.5 to 10 mm, and the flow rate at the narrowest point of the gap being 10-200 m/s. The carbon blacks of the invention can be used as non-reinforcing filler, reinforcing filler, UV stabilizer, conductive black, pigment or reducing agent.
1. Carbon black comprising an aggregate size distribution with a (d 90 -d 10 )/d 50 ratio of 0.57-0.60 and a full width at half-maximum (FWHM) to D mode ratio of 0.54-0.60 and wherein said carbon black is a gas black.
2. The carbon black of claim 1 , wherein said carbon black has a pH of less than 7.0.
3. The carbon black of claim 2 , wherein said carbon black has a volatiles content of 2.0-20.0%.
4. The carbon black of claim 3 , wherein said carbon black has a tint of 90-180%.
5. The carbon black of claim 4 , wherein said carbon black has an STSA value of 20-300 m 2 /g.
6. The carbon black of claim 1 , wherein said carbon black has a pH of less than 5.0.
7. The carbon black of claim 6 , wherein said carbon black has a volatiles content of 4.0-9.0%.
8. The carbon black of claim 7 , wherein said carbon black has a tint of 120-150%.
9. The carbon black of claim 8 , wherein said carbon black has an STSA value of 70-200 m 2 /g.
10. The carbon black of claim 1 , wherein said carbon black has a volatiles content of 2.0-20.0%.
11. The carbon black of claim 1 , wherein said carbon black has a volatiles content of 4.0-9.0%.
12. The carbon black of claim 1 , wherein said carbon black has a tint of 90-180%.
13. The carbon black of claim 1 , wherein said carbon black has a tint of 120-150%.
14. The carbon black of claim 1 , wherein said carbon black has an STSA value of 20-300 m 2 /g.
15. The carbon black of claim 1 , wherein said carbon black has an STSA value of 70-200 m 2 /g.
16. A composition comprising a carbon black according to claim 1 , wherein said composition is selected from the group consisting of: a non-reinforcing filler, a reinforcing filler, a UV stabilizer, a conductive black, a pigment, a reducing agent, rubber, plastic, a coating material, paint, paper, bitumen, concrete and other building materials.
17. The carbon black of claim 16 , wherein said carbon black:
a) has a pH of less than 7.0;
b) has a volatiles content of 2.0-20.0%; and
c) has a tint of 90-180%.
18. A composition comprising a carbon black according to claim 1 , wherein said composition is selected from the group consisting of: toner, printing ink, liquid ink, and inkjet ink.
19. The carbon black of claim 18 , wherein said carbon black:
a) has a pH of less than 7.0;
b) has a volatiles content of 2.0-20.0%; and
c) has a tint of 90-180%.
20. The carbon black of claim 18 , wherein said carbon black:
a) has a pH of less than 5.0;
b) has a volatiles content of 4.0-9.0; and
c) has a tint of 120-150%.