Controlled thickness reduction for hot-dip coated, hot-rolled steel strip and installation used in this process
View Patent ↗The invention relates to a method for hot-dip coating hot-rolled steel strip, during which the steel strip passes through a pickling station, a rinsing station, a drying station, a heating furnace and then through a molten bath. The final thickness and the thickness tolerance of the hot-dip coated steel strip are achieved by a controlled thickness reduction in a roll stand in the process line. The achievement of the finished thickness is controlled by at least one thickness measuring unit at the outlet of the roll stand, and deviations upward or downward therefrom are fed back in the form of an actuating signal for actuating the roll stand in order to appropriately increase or decrease the thickness reduction. The invention also relates to an installation for producing a steel strip of the aforementioned type.
1. A method for the hot-dip coating of a hot-rolled steel strip EN 10111-DD11 to DD14 to increase its tensile strength, whereby the steel strip passes through a pickling station, a rinsing station, a drying station, a heating furnace and then a melting bath wherein the final thickness and the thickness tolerance of the hot-dip coated hot-rolled steel strip EN 10111-DD11 are achieved, after the hot-dip coated, hot-rolled steel strip EN 10111-DD11 to DD14 has cooled down to 25° C. to 55° C., by a controlled thickness reduction in a rolling-mill stand in the processing line, whereby at least one thickness gauge located in the exit of the rolling-mill stand checks whether the final thickness has been achieved and any deviations upwards or downwards are fed back as a control signal for the adjustment of the rolling-mill stand so that the thickness reduction can be correspondingly increased or decreased so that the controlled thickness reduction in the hot-dip coated, hot-rolled steel strip lies in a range of 6.5% to 10% and with such a thickness reduction, the hot-dip coated, hot-rolled steel strip EN 10111-DD11 to DD14 has a thickness tolerance relative to the center of the strip of +0.01 mm or better.
2. The method according to claim 1 wherein a thickness gauge that measures the entering thickness of the hot-dip coated, hot-rolled steel strip EN 10111-DD11 to DD14 and reports this value to the thickness regulation means of the rolling-mill stand is arranged upstream from the rolling-mill stand.
3. The method according to claim 1 wherein strip buffers are provided upstream and/or downstream from the rolling-mill stand so that the thickness regulation means can compensate for velocity fluctuations.
4. The method according to claim 1 wherein at least one of the working rolls in the rolling-mill stand is smooth or else has a structured surface with a special finish and/or a stochastic or deterministic structure.
5. The method according to claim 1 wherein the thickness is reduced in the presence of a rolling fluid.
6. The method according to claim 1 wherein the hot-dip coating is a coating with zinc or a zinc alloy.
7. The method according to claim 1 wherein the passage through the pickling station, the rinsing station, the drying station and the melting bath takes place under the exclusion of air and oxygen.
8. The method according to claim 1 wherein the controlled thickness reduction is 6.5%.
9. A method for the hot-dip coating of a hot-rolled steel strip EN 10111-DD11 to DD14 to increase its tensile strength with a zinc or aluminum alloy, whereby the steel strip passes through a pickling station, a rinsing station, a drying station, a heating furnace and then a melting bath wherein the final thickness and the thickness tolerance of the hot-dip coated hot-rolled steel strip EN 10111-DD11 to DD14 are achieved, after the hot-dip coated, hot-rolled steel strip EN 10111-DD11 to DD14 has cooled down to 25° C. to 55° C., by a controlled thickness reduction in a rolling-mill stand in the processing line, whereby at least one thickness gauge located in the exit of the rolling-mill stand checks whether the final thickness has been achieved and any deviations upwards or downwards are fed back as a control signal for the adjustment of the rolling-mill stand so that the thickness reduction can be correspondingly increased or decreased so that the controlled thickness reduction in the hot-dip coated, hot-rolled steel strip lies in a range of 6.5% to 10% and with such a thickness reduction, the hot-dip coated, hot-rolled steel strip EN 10111-DD11 to DD14 has a thickness tolerance relative to the center of the strip of +0.01 mm or better.