Method for producing manganese oxide nanoparticle dispersed material and electrode
View Patent ↗The present invention provides a method for producing a manganese oxide nanoparticle dispersed material having steps of dissolving manganese nitrate in a polyamide acid solution (Step 1); forming a coating on the surface of the substrate using the polyamide acid solution containing manganese nitrate dissolved therein (Step 2); and carbonizing the polyamide acid and depositing manganese oxide nanoparticles by subjecting the coating to a heat treatment at a temperature not less than 600° C. but not more than 1200° C. (Step 3).
1. A method for producing a manganese oxide nanoparticle dispersed material having steps of:
dissolving manganese nitrate in a polyamide acid solution;
forming a coating on the surface of the substrate using the polyamide acid solution containing manganese nitrate dissolved therein, and then imidizing the polyamide acid contained in the coating so as to form the coating into a manganese-containing polyimide coating; and
subjecting the manganese-containing polyimide coating to a heat treatment at a temperature of not less than 600° C. but not more than 1200° C. to carbonize the polyimide and deposit manganese oxide nanoparticles.
2. The production method according to claim 1 , wherein the polyamide acid solution contains dimethylacetamide as a solvent.
3. A method for producing an electrode having manganese oxide nanoparticles dispersed thereon,
the method comprising steps of:
dissolving manganese nitrate in a polyamide acid solution;
forming a coating on the surface of a porous electrode substrate using the polyamide acid solution containing manganese nitrate dissolved therein, and then imidizing the polyamide acid contained in the coating so as to form the coating into a manganese-coating polyimide coating; and
subjecting the manganese-coating polyimide coating to a heat treatment at a temperature not less than 600° C. but not more than 1200° C. to carbonize the polyimide and deposit manganese oxide nanoparticles.
4. The production method according to claim 3 , wherein the porous electrode substrate is at least one member selected from the group consisting of carbon papers, carbon nonwoven fabrics and carbon felts.
5. The production method according to claim 3 , wherein the polyimide acid solution contains dimethylacetamide as a solvent.