Thermally conductive graphite reinforced alloys
View Patent ↗Embodiments of the present invention provide composite bodies having a discontinuous graphite preform and at least one silicon-bearing metal alloy infiltrant. Embodiments of the present invention also provide methods for producing such composite bodies. The metal alloy is preferably comprised of aluminum, copper, or magnesium, or combinations thereof. Certain preferred embodiments provide at least one aluminum alloy having from about 5% silicon to about 30% silicon, more preferably from about 11% to about 13% silicon, as an alloying element. Certain presently preferred embodiments provide an aluminum-silicon eutectic composition having about 12.5% silicon. Embodiments of the invention provide composite materials be “tuned” to more closely match thermal expansion characteristics of a number of semiconductor or integrated circuit materials such as, but not limited to, silicon, alumina, aluminum nitride, gallium nitride, and gallium arsenide while also providing high thermal conductivity. Embodiments of the present invention are especially suited for use as a heat sink, a heat spreader, or both.
1. A composite body comprising a preform having discontinuous flake graphite, discontinuous particulate graphite, or both; a third phase material; and at least one silicon-bearing metal alloy infiltrant comprising about 5% to about 30% silicon in contact with at least one graphite surface wherein said surface further comprises silicon carbide.
2. The composite body of claim 1 , wherein said infiltrant comprises about 11% to about 13% silicon.
3. The composite body of claim 1 , wherein said infiltrant is selected from the group consisting of aluminum, copper, magnesium, and combinations thereof.
4. The composite body of claim 3 , wherein said copper comprises up to about 6% silicon.
5. The composite body of claim 3 , wherein said aluminum comprises about 12.5% silicon.
6. A heat sink comprising the composite body of claim 5 .
7. A heat spreader comprising the composite body of claim 5 .
8. The composite body of claim 3 , wherein said aluminum comprises about 6% to about 15% silicon.
9. The composite body of claim 1 , wherein said graphite is selected from the group consisting of milled artificial graphite, natural flake graphite, natural vein graphite, highly graphitized mesophase pitch, and combinations thereof.
10. The composite body of claim 1 having a thermal expansion coefficient of at least about 3 ppm/K up to about 12 ppm/K.
11. The composite body of claim 1 having a base plane thermal conductivity of at least about 500 W/mK to about 750 W/mK.
12. The composite body of claim 1 having a base plane thermal conductivity of at least about 200 W/mK to about 1200 W/mK.
13. The composite body of claim 1 having a transverse thermal conductivity of at least 30 W/mK and in-plane thermal conductivity of at least 400 W/mK.
14. The composite body of claim 1 having a mass density of about 2.3 g/cm 3 to about 8.0 g/cm 3 .
15. The composite body of claim 1 wherein the third phase material is selected from the group consisting of milled fiber glass, milled graphite fiber, milled carbon fiber, colloidal silica, ash particulates, ceramic particles, sodium silicate, fume silica, and combinations thereof.
16. The composite body of claim 15 wherein said colloidal silica has an average particle size of about 0.05 to about 0.5 microns.
17. The composite body of claim 15 made by vacuum processing.
18. The composite body of claim 15 having a graphite volume fraction up to about 0.75.
19. The composite body of claim 15 having a graphite volume fraction of about 0.3 to about 0.62.
20. The composite body of claim 15 having a graphite volume fraction of about 0.4 to about 0.90.
21. A heat sink comprising the composite body of claim 15 .
22. A heat spreader comprising the composite body of claim 15 .
23. A heat sink comprising the composite body of claim 1 .
24. A heat spreader comprising the composite body of claim 1 .
25. A composite body comprising a preform having:
discontinuous flake graphite, discontinuous particulate graphite, or both;
a third phase material selected from the group consisting of milled fiber glass, milled graphite fiber, milled carbon fiber, colloidal silica, ash particulates, ceramic particles, fume silica, sodium silicate, and combinations thereof; and
at least one silicon-bearing metal alloy infiltrant comprising about 5% to about 30% silicon in contact with at least one graphite surface.
26. The composite body of claim 25 further being resistant to deformation during pressure infiltration.
27. The composite body of claim 25 , wherein said graphite is selected from the group consisting of milled artificial graphite, natural flake graphite, natural vein graphite, highly graphitized mesophase pitch, and combinations thereof.
28. The composite body of claim 25 , wherein said infiltrant comprises aluminum having about 6 to about 15% silicon.
29. The composite body of claim 25 , wherein said infiltrant comprises aluminum having about 5 to about 30% silicon.
30. The composite body of claim 25 , wherein said infiltrant comprises aluminum having about 11% to about 13% silicon.
31. The composite body of claim 25 , wherein said infiltrant comprises aluminum having about 12.5% silicon.
32. The composite body of claim 25 , wherein said infiltrant comprises copper having up to about 6% silicon.
33. The composite body of claim 25 having a graphite volume fraction of about 0.40 to about 0.90.
34. The composite body of claim 25 having a graphite volume fraction of about 0.32 to about 0.62.