Alkaline electrochemical cell having a negative electrode with solid zinc oxide and a surfactant
View Patent ↗An alkaline electrochemical cell comprising a negative electrode, wherein the negative electrode includes zinc as an active material and further includes a synergistic combination of a solid zinc oxide and a surfactant. More particularly, the invention discloses an alkaline electrochemical cell that is capable of providing improved service when utilized by high drain devices.
1. A primary alkaline electrochemical cell, comprising:
a container;
an electrode assembly disposed within the container and comprising a positive electrode, a negative electrode, a separator located between the positive electrode and the negative electrode, and an alkaline electrolyte, wherein the negative electrode comprises zinc, solid zinc oxide and a surfactant adsorbed on a surface of the solid zinc oxide, wherein the surfactant comprises a water soluble block copolymer, and wherein the block copolymer has at least one anionic functional group and at least one nonionic functional group; and
wherein the zinc is present in an amount from 64 to 68 weight percent based on the total weight of the negative electrode, wherein the solid zinc oxide is present in an amount from 1.5 to 5.0 weight percent based on the total weight of the negative electrode, wherein the solid zinc oxide has a BET surface area greater than 20 m 2 /g, wherein the solid zinc oxide has a D50 particle size greater than 2 microns, and wherein the surfactant is present in an amount from 0.00064 to 0.20 weight percent based on the total weight of the negative electrode.
2. The cell according to claim 1 , wherein the block copolymer has a number average molecular weight greater than 1000.
3. The cell according to claim 1 , wherein the solid zinc oxide is present in an amount from 2 to 3 weight percent based on the total weight of the negative electrode and wherein the negative electrode further comprises dissolved zinc oxide.
4. The cell according to claim 3 , wherein the solid zinc oxide has a BET surface area greater than 40 m 2 /g, wherein the negative electrode includes a gelling agent and wherein the positive electrode comprises manganese dioxide.
5. A primary alkaline electrochemical cell, comprising:
a container;
an electrode assembly disposed within the container and comprising a positive electrode comprising manganese dioxide, a negative electrode, a separator located between the positive electrode and the negative electrode, and an alkaline electrolyte, wherein the negative electrode comprises zinc, solid zinc oxide and a surfactant comprising a water soluble block copolymer, and wherein the solid zinc oxide has a BET surface area greater than 20 m 2 /g; and
wherein the zinc is present in an amount from 64 to 68 weight percent based on the total weight of the negative electrode, wherein the solid zinc oxide is present in an amount from 1.5 to 5.0 weight percent based on the total weight of the negative electrode, wherein the solid zinc oxide has a D50 particle size greater than 2 microns, wherein the surfactant is present in an amount from 0.00064 to 0.20 weight percent based on the total weight of the negative electrode, and wherein the block copolymer has at least one anionic functional group.
6. The cell according to claim 5 , wherein the block copolymer has at least two different functional groups and a number average molecular weight greater than 1000.
7. The cell according to claim 5 , wherein the solid zinc oxide is present in an amount from 2 to 3 weight percent based on the total weight of the negative electrode and wherein the negative electrode further comprises dissolved zinc oxide.
8. A primary alkaline electrochemical cell, comprising:
a container;
an electrode assembly disposed within the container and comprising a positive electrode comprising manganese dioxide, a negative electrode, a separator located between the positive electrode and the negative electrode, and an alkaline electrolyte, wherein the negative electrode comprises zinc, solid zinc oxide and a surfactant comprising a water soluble block copolymer having at least two different types of functional groups, wherein the zinc is present is an amount from 64 to 68 weight percent, wherein the solid zinc oxide is present in an amount from 1.5 to 5.0 weight percent, and wherein the surfactant is present in an amount from 0.00064 to 0.20 weight percent, wherein all weight percents are based on the total weight of the negative electrode; and
wherein the solid zinc oxide has a BET surface area greater than 20 in 2 /g and wherein the solid zinc oxide has a D50 particle size greater than 2 microns.
9. The cell according to claim 8 , wherein the solid zinc oxide is present in an amount from 2 to 3 weight percent based on the total weight of the negative electrode and wherein the negative electrode further comprises dissolved zinc oxide.
10. The cell according to claim 9 , wherein the block copolymer has a number average molecular weight greater than 1000 and wherein the block copolymer has at least one anionic functional group and at least one nonionic functional group.