Low temperature curable melamine containing coating composition and the use thereof
View Patent ↗The present invention is directed to a melamine containing coating composition curable at ambient temperatures and suitable for coating plastic substrates. The present invention is also directed to a process for coating plastic substrates with a melamine containing coating composition curable at ambient temperatures.
1. A coating composition curable at ambient temperatures, said coating composition consisting of:
(A) a crosslinkable component consisting of 15 to 99 weight percent of total solid weight of the crosslinkable component a polyester having hydroxyl crosslinkable groups and a weight average molecular weight in a range of from 1500 to 100,000, and 1 to 15 weight percent of total solid weight of the crosslinkable component a melamine having crosslinkable groups selected from an —NH group, a hydroxyl group, or a combination thereof;
(B) a crosslinking component consisting of a polyisocyanate compound having two or more isocyanate groups that react with the crosslinkable groups at ambient temperatures in a range of from 40° F. (4° C.) to 200° F. (93° C.);
(C) one or more pigments or effect pigments; and
(D) one or more additives selected from conductive additives, viscosity adjuster, catalyst, one or more solvents, or a combination thereof;
wherein said coating composition is formulated as a primer, or a color matched primer.
2. The coating composition of claim 1 , wherein the polyisocyanate compound is a diisocyanate, a diisocyanate trimer, a triisocyanate, a triisocyanate trimer, or a combination thereof.
3. The coating composition of claim 1 , wherein the melamine is selected from monomeric melamine, alkylated melamine, polymeric melamine-formaldehyde resin, alkylated polymeric melamine-formaldehyde resin, or a combination thereof.
4. A coated plastic substrate coated with the coating composition of claim 1 .
5. A coating composition curable at ambient temperatures, said coating composition consisting of:
(A) a crosslinkable component consisting of 15 to 99 weight percent of total solid weight of the crosslinkable component a polyester having hydroxyl crosslinkable groups and a weight average molecular weight in a range of from 1500 to 100,000, and 1 to 15 weight percent of total solid weight of the crosslinkable component a melamine having crosslinkable groups selected from an —NH group, a hydroxyl group, or a combination thereof;
(B) a crosslinking component consisting of a polyisocyanate compound having two or more isocyanate groups that react with the crosslinkable groups at ambient temperatures in a range of from 40° F. (4° C.) to 200° F. (93° C.);
(C) one or more pigments or effect pigments;
(D) one or more additives selected from conductive additives, viscosity adjuster, catalyst, one or more solvents, or a combination thereof; and
(E) acrylic polymers, reactive oligomers, or a combination thereof.