Method for surface treatment of titanium dioxide pigment
View Patent ↗A method of preparing coated titanium dioxide particles is provided. The method can include forming an aqueous suspension of titanium dioxide particles having a pH of from about 5.0 to about 7.0; adding a zirconium oxide-forming solution to the suspension in an amount sufficient to decrease the pH of the suspension to about 4.0 or lower; forming a zirconium oxide coating on the titanium dioxide particles to form a suspension of coated particles; adding an aluminum oxide-forming solution to the suspension of coated particles in an amount sufficient to increase the pH of the suspension to about 9.0 or higher; and forming an aluminum oxide coating on the coated particles to form a product.
1. A method for preparing a coated titanium dioxide pigment, comprising:
(a) forming an aqueous suspension of titanium dioxide particles having a pH of from about 5.0 to about 7.0;
(b) adding an aluminum oxide-forming solution to the suspension of particles in an amount sufficient to increase the pH of the suspension to about 9.0 or higher, the aluminum oxide-forming solution comprising a water-soluble aluminum oxide-forming compound and water and being free of any additional pH-adjusting compounds other than the water-soluble aluminum oxide-forming compound; and
(c) forming an aluminum oxide coating on the titanium dioxide particles;
wherein the method is free of adding any additional pH-adjusting compounds other than the water-soluble aluminum oxide-forming compound.
2. The method of claim 1 , wherein the aluminum oxide-forming solution comprises sodium aluminate.
3. The method of claim 1 , consisting essentially of steps (a)-(c).
4. The method of claim 1 , consisting of steps (a)-(c).
5. A method for preparing a coated titanium dioxide pigment, comprising:
(a) forming an aqueous suspension of titanium dioxide particles having a pH of from about 5.0 to about 7.0;
(b) adding a zirconium oxide-forming solution to the suspension in an amount sufficient to decrease the pH of the suspension to about 4.0 or lower, the zirconium oxide-forming solution comprising a water-soluble zirconium oxide-forming compound and water and being free of any additional pH-adjusting compounds other than the water-soluble zirconium oxide-forming compound;
(c) forming a zirconium oxide coating on the titanium dioxide particles to form a suspension of coated particles;
(d) adding an aluminum oxide-forming solution to the suspension of coated particles in an amount sufficient to increase the pH of the suspension to about 9.0 or higher, the aluminum oxide-forming solution comprising a water-soluble aluminum oxide-forming compound and water and being free of any additional pH-adjusting compounds other than the water-soluble aluminum oxide-forming compound; and
(e) forming an aluminum oxide coating on the coated particles to form a product;
wherein the method is free of adding any additional pH-adjusting compounds other than the water-soluble zirconium oxide-forming compound and the water-soluble aluminum oxide-forming compound.
6. The method of claim 5 , wherein the pH of the aqueous suspension of titanium dioxide particles before adding the zirconium oxide-forming solution in step (b) is from about 5.5 to about 6.5.
7. The method of claim 5 , wherein the pH of the aqueous suspension of titanium dioxide particles before adding the water-soluble zirconium oxide-forming compound in step (b) is about 6.0.
8. The method of claim 5 , wherein the amount of the zirconium oxide-forming solution added in step (b) is sufficient to cause the pH of the aqueous suspension of titanium dioxide particles after adding the water-soluble zirconium oxide-forming solution to be about 3.0 or lower.
9. The method of claim 5 , wherein the pH of the aqueous suspension of titanium dioxide particles after adding the aluminum oxide-forming solution in step (d) is about 9.5 or higher.
10. The method of claim 5 , wherein the titanium dioxide particles in step (a) have an average particle diameter in a range of from about 0.01 micron to about 1.0 micron.
11. The method of claim 5 , wherein the titanium dioxide particles in step (a) have an average particle diameter of less than or equal to about 0.2 micron.
12. The method of claim 5 , wherein the aqueous suspension of titanium dioxide particles has a concentration in a range of from about 10% to about 50%.
13. The method of claim 5 , wherein the zirconium oxide-forming solution comprises a zirconium chloride.
14. The method of claim 5 , wherein the zirconium oxide-forming solution comprises zirconium orthosulfate.
15. The method of claim 5 , wherein the aluminum oxide-forming solution comprises sodium aluminate.
16. The method of claim 5 , further comprising after step (e):
(f) filtering the aqueous suspension to recover the product; and
(g) washing and drying the recovered product.
17. The method of claim 16 , wherein the final pH of the washed product is about 6.0.
18. The method of claim 5 , wherein the zirconium oxide coating is formed on the titanium dioxide particles in step (c) over a time period of at least 10 minutes.
19. The method of claim 5 , wherein the aluminum oxide coating is formed on the coated titanium dioxide particles in step (e) over a time period of at least 10 minutes.
20. The method of claim 5 , wherein the zirconium oxide-forming solution consists of zirconium ortho-sulphate and water.
21. The method of claim 5 , wherein the zirconium oxide-forming solution consists of zirconium ortho-sulphate and water, and the aluminum oxide-forming solution comprises sodium aluminate.
22. A method for preparing a coated titanium dioxide pigment, consisting essentially of:
(a) forming an aqueous suspension of titanium dioxide particles having a pH of from about 5.0 to about 7.0;
(b) adding a zirconium oxide-forming solution to the suspension in an amount sufficient to decrease the pH of the suspension to about 4.0 or lower, the zirconium oxide-forming solution comprising a water-soluble zirconium oxide-forming compound and water and being free of any additional pH-adjusting compounds other than the water-soluble zirconium oxide-forming compound;
(c) forming a zirconium oxide coating on the titanium dioxide particles to form a suspension of coated particles;
(d) adding an aluminum oxide-forming solution to the suspension of coated particles in an amount sufficient to increase the pH of the suspension to about 9.0 or higher, the aluminum oxide-forming solution comprising a water-soluble aluminum oxide-forming compound and water and being free of any additional pH-adjusting compounds other than the water-soluble aluminum oxide-forming compound; and
(e) forming an aluminum oxide coating on the coated particles to form a product;
wherein the method is free of adding any additional pH-adjusting compounds other than the water-soluble zirconium oxide-forming compound and the water-soluble aluminum oxide-forming compound.
23. The method of claim 22 , wherein the zirconium oxide-forming solution comprises zirconium orthosulfate.
24. The method of claim 22 , wherein the method consists of steps (a) through (e).