Modification of polyethylene with ozone
View Patent ↗A method of modifying polyethylene is disclosed. The method comprises contacting the polyethylene powder with ozone. The modified polyethylene exhibits an increase in melt elasticity and the complex viscosity at low shear rates. The rheological benefits are achieved without a significant reduction in the weight average molecular weight of the polyethylene. The modified polyethylene can be used in applications that require higher melt strength such as film or blow molding.
1. A method of modifying a polyethylene, which comprises contacting a polyethylene powder having an initial weight average molecular weight (Mw) within the range from about 35,000 to about 3,500,000, at a temperature within the range of about 20° C. to about 80° C., with a contacting time within the range from about 30 minutes to about 8 hours, with ozone wherein the ozone concentration is within the range of about 0.01 wt % to about 200 wt % of the polyethylene, to produce a modified polyethylene having reduced weight average molecular weight (Mw) by less than 20% and increased melt elasticity (ER) by at least 10%.
2. The method of claim 1 wherein the ozone concentration is within the range of about 6 wt % to about 100 wt % of the polyethylene.
3. The method of claim 1 wherein the temperature is within the range of about 25° C. to about 55° C.
4. The method of claim 1 wherein the temperature is within the range of about 25° C. to about 35° C.
5. The method of claim 1 wherein the Mw reduction is less than 10%.
6. The method of claim 1 wherein the Mw reduction is less than 5%.
7. The method of claim 1 wherein the ER increase is greater than 15%.
8. The method of claim 1 wherein the ER increase is greater than 50%.
9. The method of claim 1 wherein the polyethylene is a bimodal, high density polyethylene.
10. The method of claim 1 wherein the modified polyethylene has an increase in complex viscosity (η*) by at least 5%.
11. The method of claim 10 wherein the increase in η* is at least 15%.