Sliding part and method of manufacturing the same
View Patent ↗A sliding part in which a surface coverage ratio of copper in the sliding part increases. A bearing which is the sliding part is formed by filling the raw powder into the filling portion of the forming mold, compacting the raw powder to form a powder compact, and sintering the powder compact. A copper-based raw powder is composed of a copper-based flat raw powder having an average diameter smaller than that of an iron-based raw powder and an aspect ratio larger than that of the iron-based raw powder, and a copper-based small-sized raw powder having the average diameter is smaller than that of the copper-based flat raw powder. The copper segregates at the surface of the sliding part. In the bearing in which the copper-based flat powder segregates at the surface, the surface is covered with the copper-based small-sized raw powder that has emerged on the surface, as well as the copper-based flat raw powder, thereby it is possible to increase the surface coverage ratio of copper. Furthermore, containing calcium fluoride improves the seizure resistance.
1. A sliding part formed by sintering a powder compact, which is fabricated by filling an iron-based raw powder and a copper-based raw powder into a filling portion of a forming mold and compacting the raw powders,
wherein the copper-based raw powder is comprised of a copper-based flat raw powder having an average diameter smaller than that of the iron-based raw powder and an aspect ratio larger than that of the iron-based raw powder, and a copper-based small-sized raw powder having an average diameter smaller than that of the copper-based flat raw powder; and
copper segregates on a surface of the sliding part and calcium fluoride is dispersed and distributed in a basis material.
2. The sliding part according to claim 1 ,
wherein a surface coverage ratio of copper is 80% or more.
3. The sliding part according to claim 1 ,
wherein the aspect ratio of the copper-based flat raw powder is 10 or more.
4. The sliding part according to claim 2 ,
wherein a ratio of the copper-based raw powder is 20 to 40% by weight with respect to all raw powders.
5. A sliding part formed by sintering a powder compact, which is fabricated by filling an iron-based raw powder and a copper-based raw powder into a filling portion of a forming mold and compacting the raw powders,
wherein the copper-based raw powder is comprised of a copper-based flat raw powder having an average value of a maximum projected area smaller than that of the maximum projected area of the iron-based raw powder and an aspect ratio larger than that of the iron-based raw powder, and a copper-based small-sized raw powder having an average value of a maximum projected area smaller than that of the maximum projected area of the copper-based flat raw powder; and
copper segregates on a surface of the sliding part and calcium fluoride is dispersed and distributed in a basis material.
6. The sliding part according to claim 5 ,
wherein a surface coverage ratio of copper is 80% or more.
7. A method of manufacturing a sliding part comprising the scope of;
filling an iron-based raw powder and a copper-based raw material into a filling portion of a forming mold,
compacting the raw powders to form a powder compact, and
sintering the powder compact;
wherein calcium fluoride as well as the iron-based raw powder and the copper-based raw powder are filled into a filling portion, the copper-based raw powder is comprised of a copper-based flat raw powder having an average diameter smaller than that of the iron-based raw powder and an aspect ratio larger than that of the iron-based raw powder; and a copper-based small-sized raw powder having an average diameter smaller than that of the copper-based flat raw powder, and
copper segregates on a surface of the sliding part.
8. A method of manufacturing a sliding part comprising the scope of;
filling an iron-based raw powder and a copper-based raw material into a filling portion of a forming mold,
compacting the raw powders to form a powder compact, and
sintering the powder compact;
wherein calcium fluoride as well as the iron-based raw powder and the copper-based raw powder are filled into a filling portion, the copper-based raw powder is comprised of a copper-based flat raw powder having an average value of a maximum projected area smaller than that of the maximum projected area of the iron-based raw powder and an aspect ratio larger than that of the iron-based raw powder; and a copper-based small-sized raw powder having an average value of a maximum projected area smaller than that of the maximum projected area of the copper-based flat raw powder, and
copper segregates on a surface of the sliding part.
9. The method according to claim 7 ,
wherein the aspect ratio of the copper-based flat raw powder is 10 or more.
10. The method according to any one of claim 7 ,
wherein a ratio of the copper-based raw powder is 20 to 40% by weight with respect to all raw powders.
11. The method according to claim 8 ,
wherein the aspect ratio of the copper-based flat raw powder is 10 or more.
12. The method according to any one of claim 8 ,
wherein a ratio of the copper-based raw powder is 20 to 40% by weight with respect to all raw powders.