High melt flow polymer of improved durability for pipe applications

1. A polymer composition, comprising

(i) a polypropylene homopolymer having a melt flow rate MFR 2.16 kg/230° C. of less than 20 g/10 min,

(ii) a polypropylene random copolymer, prepared by copolymerization of propylene with an olefin comonomer and having an amount of olefin comonomer units of 0.2 to 5.0 wt %, and

(iii) an elastomeric copolymer of propylene and at least one olefin comonomer, comprising from 10 to 50 wt % olefin comonomer units based on the weight of the elastomeric copolymer,

wherein the polymer composition has a tensile modulus, determined according to ISO 527-2/1 B at 1 mm/min. and 23° C., of at least 1400 MPa;

wherein the polymer composition has a melting point of from 155.6° C. to less than 164° C.; and

wherein the polypropylene homopolymer and the polypropylene random copolymer are blended during polymerization to result in a polypropylene-based matrix.

2. The polymer composition according to claim 1 , wherein the weight average molecular weight of the polypropylene random copolymer is higher than the weight average molecular weight of the polypropylene homopolymer.

3. The polymer composition according to claim 1 , wherein the olefin comonomer of the polypropylene random copolymer is selected from ethylene, C 4 to C 10 alpha-olefins, or mixtures thereof.

4. The polymer composition according to claim 3 , wherein the olefin comonomer is ethylene.

5. The polymer composition according to claim 4 , wherein the polypropylene random copolymer comprises an amount of 0.2 to 3.0 wt % of ethylene comonomer units.

6. The polymer composition according to claim 1 , wherein the amount of olefin comonomer units within the polypropylene random copolymer is from 0.1 wt % to 3.0 wt %, based on the combined weight of the polypropylene homopolymer and the polypropylene random copolymer fraction.

7. The polymer composition according to claim 1 , wherein the polypropylene-based matrix has a melt flow rate MFR 2.16 kg/230° C. within the range of 0.1 g/10 min. to 10.0 g/10 min.

8. The polymer composition according to claim 1 , wherein the olefin comonomer of the elastomeric copolymer is selected from ethylene, C 4 to C 10 alpha-olefins, or mixtures thereof.

9. The polymer composition according to claim 8 , wherein the olefin comonomer is ethylene.

10. The polymer composition according to claim 1 , having a melt flow rate MFR 2.16 kg/230° C. and a resistance to slow crack growth which satisfy the following relationship:

t≧ 300−(200*MFR 2.16 kg/230° C. ) for 0.1 g/10 min≦MFR 2.16 kg/230° C. <1.0 g/10 min,

t≧ 105−(5*MFR 2.16 kg/230° C. ) for 1.0 g/10 min≦MFR 2.16 kg/230° C. <10.0 g/10 min,

t≧ 55 for MFR 2.16 kg/230° C. ≧10.0 g/10 min,

wherein t in hours is the time of failure in the slow crack growth test performed at 80° C. and 4.2 MPa according to ISO 1167.

11. The polymer composition according to claim 1 , having a melt flow rate MFR 2.16 kg/230° C. of at least 0.2 g/10 min.

12. The polymer composition according to claim 11 , having a melt flow rate MFR 2.16 kg/230° C. of at least 0.2 g/10 min but less than 10.0 g/10 min.

13. The polymer composition according to claim 1 , comprising the elastomeric copolymer in an amount of 5 to 15 wt %.

14. The polymer composition according to claim 1 , having a Charpy impact strength of at least 2.0 kJ/m 2 , measured according to ISO 179/1 eA at −20° C.

15. The polymer composition according to claim 14 , wherein the tensile modulus is at least 1375 MPa and the Charpy impact strength at −20° C. is at least 3.0 kJ/m 2 .

16. The polymer composition according to claim 1 , further comprising a nucleating agent selected from talc, polymerized vinyl compounds, dibenzylidene sorbitol, sodium benzoate, di(alkylbenzylidene)sorbitol, or mixtures thereof.

17. The polymer composition according to claim 16 , wherein the nucleating agent is a polymerized vinyl compound.

18. The polymer composition according to claim 1 , wherein the polymer composition has a polydispersion index from 2.5 to 6.0.

19. A polymer composition, consisting of:

(i) a polypropylene homopolymer having a melt flow rate MFR 2.16kg/230° C. of less than 20 g/10 min,

(ii) a polypropylene random copolymer, prepared by copolymerization of propylene with an olefin comonomer and having an amount of olefin comonomer units of 0.2 to 5.0 wt %, and

(iii) an elastomeric copolymer of propylene and at least one olefin comonomer, comprising from 10 to 50 wt % olefin comonomer units based on the weight of the elastomeric copolymer,

wherein the polymer composition has a tensile modulus, determined according to ISO 527-2/1 B at 1 mm/min. and 23° C., of at least 1400 MPa; and

wherein the polymer composition has a melting point from greater than 157° C. to less than 164° C.