Polyester Resin Composition for Covering Material of Cable and Cable Using the Same
Disclosed is a polyester resin composition for a covering material of a cable. The present invention provides the polyester resin composition for a covering material of a cable including a polyester resin as a base resin, including 0.1 to 4 parts by weight of amide-based wax as an internal lubricant, based on 100 parts by weight of the polyester resin as the base resin. The polyester resin composition according to the present invention has advantages that the resin may be uniformly and completely melted using only the general equipments such as an extruder with an L/D ratio of less than 30 and a single-stranded screw without an additional investment for equipments, and also has such an improved processability that protrusions are minimized upon forming a covering layer of a cable, as well as an excellent mechanical properties such as tensile strength, elongation, etc.
1 . A polyester resin composition for a covering material of a cable including a polyester resin as a base resin, comprising 0.1 to 4 parts by weight of amide-based wax as an internal lubricant, based on 100 parts by weight of the polyester resin as the base resin.
2 . The polyester resin composition for a covering material of a cable according to claim 1 ,
wherein the polyester resin is at least one selected from the group consisting of polyethyleneterephthalate (PET), polybutyleneterephthalate (PBT) and thermoplastic elastomer-ester (TPE-E) copolymers thereof.
3 . The polyester resin composition for a covering material of a cable according to claim 1 ,
wherein the amide-based wax is at least one selected from the group consisting of TR-016 and TR-065 (Strucktol), Armoslip (Akzo) and LC140 (Lion Chemtec).
4 . The polyester resin composition for a covering material of a cable according to claim 1 , further comprising 0.1 to 4 parts by weight of a fluorine-based processing aid, based on 100 parts by weight of the base resin.
5 . The polyester resin composition for a covering material of a cable according to claim 4 ,
wherein the fluorine-based processing aid is at least one selected from the group consisting of Dynamar (3M), Viton FreeFlow (Dupont-Dow) and mixtures thereof.
6 . A cable that includes a conductor bundle; and a covering layer surrounding the conductor bundle,
wherein the covering layer is formed of the composition as defined claim 1 .
7 . A cable that includes a conductor bundle; and a covering layer surrounding the conductor bundle,
wherein the covering layer is formed of the composition as defined in claim 2 .
8 . A cable that includes a conductor bundle; and a covering layer surrounding the conductor bundle,
wherein the covering layer is formed of the composition as defined in claim 3 .
9 . A cable that includes a conductor bundle; and a covering layer surrounding the conductor bundle,
wherein the covering layer is formed of the composition as defined in claim 4 .
10 . A cable that includes a conductor bundle; and a covering layer surrounding the conductor bundle,
wherein the covering layer is formed of the composition as defined in claim 5 .