Steam reforming
A process for the steam reforming of hydrocarbons comprises partially oxidising a feedgas comprising a hydrocarbon feedstock with an oxygen-containing gas in the presence of steam to form a partially oxidised hydrocarbon gas mixture at a temperature >1200° C. and passing the resultant partially oxidised hydrocarbon gas mixture through a bed of steam reforming catalyst, wherein the bed comprises a first layer and a second layer, each layer comprising a catalytically active metal on an oxidic support wherein the oxidic support for the first layer is a zirconia.
1. A process for the steam reforming of hydrocarbons comprising;
(i) partially combusting a feedgas comprising a hydrocarbon feedstock with an oxygen-containing gas in the presence of steam in a combustion zone using a burner apparatus to form a partially combusted hydrocarbon gas mixture at a temperature >1200° C. and
(ii) subjecting the resultant partially combusted hydrocarbon gas mixture from the combustion zone to a steam reforming process by passing it adiabatically through a bed of steam reforming catalyst disposed below the burner apparatus, the bed of steam reforming catalyst comprising a first layer and a second layer, wherein the partially combusted hydrocarbon gas mixture is passed through the first layer and then the second layer, each layer comprising a catalytically active metal on an oxidic support wherein the catalytically active metal in the first layer is selected from the group consisting of platinum, palladium, iridium, ruthenium or rhodium, the oxidic support for the first layer is a zirconia, the catalytically active metal in the second layer is nickel and the oxidic support for the second layer is a refractory support selected from the group consisting of zirconia, alumina, calcium aluminate, magnesium aluminate, titania, magnesia and a mixture thereof, wherein a layer of zirconia balls, pellets or tiles is placed on top of the first layer of reforming catalyst.
2. A process according to claim 1 wherein at least one of the first layer and the second layer reforming catalysts are particulate, or comprise one or more monolithic supports.
3. A process according to claim 1 wherein the catalytically active metal in the first layer of steam reforming catalyst is rhodium.
4. A process according to claim 1 wherein the oxidic support for the second layer is alumina or a calcium- or magnesium-aluminate.
5. A process according to claim 1 wherein the first layer of steam reforming catalyst has a higher geometric surface area than the second layer of steam reforming catalyst.
6. A process according to claim 1 wherein the second layer comprises two or more successive layers of a steam reforming catalyst including a third and a further layer, the third or the further layer having a lower catalytic activity than that preceding it.
7. A process according to claim 1 wherein the catalytically active metal in the first layer of steam reforming catalyst is rhodium or platinum.
8. A process according to claim 1 , wherein the steam to carbon ratio of the gas fed to the steam reforming process is in the range 0.5 to 2.
9. A process according to claim 1 wherein the thickness of the bed of steam reforming catalyst is in the range 3-5 meters.
10. A process according to claim 1 wherein the first layer comprises between 3 and 25% of the thickness of the bed.
11. A process according to claim 1 wherein the first layer comprises between 5 and 15% of the thickness of the bed.
12. A process according to claim 1 wherein the first layer comprises rhodium on zirconia and the second layer comprises nickel on alumina or magnesium- or calcium-aluminate.
13. A process according to claim 1 wherein the thickness of the bed of steam reforming catalyst is in the range 1-10 meters.
14. A process according to claim 1 wherein with the first layer comprises between 1 and 50% of the thickness of the bed.