Mixed oxide powder comprising alkali metal oxide, and silicone rubber comprising this powder

1. A mixed oxide powder comprising: from 0.005 to 5% by weight of at least one alkali metal oxide and at least one metal oxide, wherein the powder

is in the form of aggregates of pore-free primary particles,

has a BET surface area of from 100 to 350 m 2 /g,

has a specific DBP number, expressed as DBP number per square meter of specific surface area, greater than or equal to that of a powder which has only the metal oxide component, and

has the alkali metal oxide distributed in the core and on the surface of the primary particles.

2. The mixed oxide powder according to claim 1 , wherein the DBP number per square metre of specific surface area is greater than 1.14.

3. The mixed oxide powder according to claim 1 , wherein potassium or sodium are the alkali metal of the alkali metal oxide.

4. The mixed oxide powder according to claim 1 , characterized in that wherein silicon dioxide is the metal oxide.

5. The mixed oxide powder according to claim 1 , wherein the powder has a specific surface area of 200±25 m 2 /g or 300±25 m 2 /g.

6. The mixed oxide powder according to claim 1 , wherein a 4% dispersion of the powder in water has a pH of less than 5.

7. The mixed oxide powder according to claim 1 , wherein the content of alkali metal oxide is from 0.05 to 0.3% by weight.

8. A process for production of the mixed metal oxide powder of claim 1 , comprising:

producing an aerosol via spraying of a solution or dispersion of at least one metal salt;

carrying the aerosol by means of a carrier gas stream through an externally heated line and thus heated to from 100° C. to 120° C., the carrier gas stream directed in such a way that it initially impacts, laterally with respect to the nozzle, the base of a plate, on which the nozzle has been mounted;

mixing homogeneously the aerosol with a gas mixture comprising at least one metal compound and whose metal component differs from the metal component of the aerosol, and with a combustion gas and oxygen, the amount of the aerosol introduced here into the gas mixture being such that the subsequent product comprises from 0.005 to 5% by weight of the metal oxide derived from the aerosol; and

igniting the aerosol-gas mixture and allowing the mixture to complete reaction in a flame and isolating the resultant powder from the exhaust gas stream.

9. The process according to claim 8 , wherein the metal salt is an alkali metal salt.

10. The process according to claim 9 , wherein the concentration of the metal salt solution is from 0.5 to 25% by weight.

11. A silicone rubber, comprising the mixed oxide powder according to claim 1 .