In order to provide an alkaline dry battery which enables to improve the operational stability of digital equipment by suppressing the progress of polarization during heavy load pulse discharge while maintaining the excellent heavy load discharge characteristics, and has an excellent reliability in terms of the leakage resistance and the safety under short-circuit conditions, the alkaline dry battery includes a positive electrode including a nickel oxyhydroxide powder and a manganese dioxide powder as positive electrode active materials, and including graphite as a conductive material; a negative electrode including zinc or a zinc alloy as a negative electrode active material; a separator interposed between the positive electrode and the negative electrode; a negative electrode current collector inserted in the negative electrode; an aqueous alkaline solution included in the separator; a battery case housing the positive electrode, the negative electrode, the separator, the negative electrode current collector and the aqueous alkaline solution; a sealing member for sealing an opening of the battery case, wherein the positive electrode includes a calcium compound in an amount of 0.1 to 10 mol % relative to a total amount of the positive electrode active material, and the content of iron element in the calcium compound is 150 ppm or less.
1 . An alkaline dry battery comprising: a positive electrode including a nickel oxyhydroxide powder and a manganese dioxide powder as positive electrode active materials, and including graphite as a conductive material; a negative electrode including zinc or a zinc alloy as a negative electrode active material; a separator interposed between said positive electrode and said negative electrode; a negative electrode current collector inserted in said negative electrode; an aqueous alkaline solution included in said separator; a battery case housing said positive electrode, said negative electrode, said separator, said negative electrode current collector and said aqueous alkaline solution; a sealing member for sealing an opening of said battery case, wherein
said positive electrode includes a calcium compound in an amount of 0.1 to 10 mol % relative to a total amount of said positive electrode active material, and the content of iron element in said calcium compound is 150 ppm or less.
2 . The alkaline dry battery in accordance with claim 1 , wherein said calcium compound is a calcium oxide or calcium hydroxide.
3 . The alkaline dry battery in accordance with claim 1 , wherein said nickel oxyhydroxide powder has a mean nickel valence of 2.95 or more.
4 . The alkaline dry battery in accordance with claim 1 , wherein said nickel oxyhydroxide powder has a mean particle size of 8 to 18 μm.
5 . The alkaline dry battery in accordance with claim 1 , wherein the weight ratio between said nickel oxyhydroxide powder and said manganese dioxide powder is 20:80 to 90:10.
6 . The alkaline dry battery in accordance with claim 1 , wherein the weight ratio between said nickel oxyhydroxide powder and said manganese dioxide powder is 20:80 to 60:40.
7 . The alkaline dry battery in accordance with claim 1 , wherein said nickel oxyhydroxide powder is a powder obtained by oxidizing a nickel hydroxide powder having a half-width of 0.6 to 0.8 deg./2θ of the (101) plane and a half-width of 0.5 to 0.7 deg./2θ of the (001) plane in powder X-ray diffraction.
8 . The alkaline dry battery in accordance with claim 2 , wherein said nickel oxyhydroxide powder has a mean nickel valence of 2.95 or more.
9 . The alkaline dry battery in accordance with claim 2 , wherein said nickel oxyhydroxide powder has a mean particle size of 8 to 18 μm.
10 . The alkaline dry battery in accordance with claim 2 , wherein the weight ratio between said nickel oxyhydroxide powder and said manganese dioxide powder is 20:80 to 90:10.
11 . The alkaline dry battery in accordance with claim 2 , wherein the weight ratio between said nickel oxyhydroxide powder and said manganese dioxide powder is 20:80 to 90:10.
12 . The alkaline dry battery in accordance with claim 2 , wherein said nickel oxyhydroxide powder is a powder obtained by oxidizing a nickel hydroxide powder having a half-width of 0.6 to 0.8 deg./2θ of the (101) plane and a half-width of 0.5 to 0.7 deg./2θ of the (001) plane in powder X-ray diffraction.