Method for reducing and/or refining a metal-containing slag
View Patent ↗The invention relates to a method for reducing and/or refining a metal-containing slag. The aim of the invention is to improve reduction of the slag. For this purpose, calcium carbide (CaC 2 ) is added to the slag as the reducing agent.
1. A method for reducing and/or cleaning a metal-bearing slag, where calcium carbide (CaC 2 ) is used as a reducing agent and slag is added to the calcium carbide (CaC 2 ), wherein the calcium carbide (CaC 2 ) is charged into a furnace before molten slag is charged into the furnace, wherein the calcium carbide (CaC 2 ) is added in an amount of 0.1% to 2.0% of the mass of the slag.
2. A method in accordance with claim 1 , wherein the calcium carbide (CaC 2 ) is added in an amount of 0.5% to 1.5% of the mass of the slag.
3. A method in accordance with claim 1 , wherein besides the calcium carbide (CaC 2 ), additional reducing agents are added.
4. A method in accordance with claim 3 , wherein a solid substance, especially coke, charcoal and/or pig iron, is used as the additional reducing agent.
5. A method in accordance with claim 3 , wherein a carbon-bearing substance, especially bunker fuel oil, diesel oil, natural gas, and/or coal dust is used as the additional reducing agent.
6. A method in accordance with claim 3 , wherein the additional reducing agent is injected into the molten slag.
7. A method in accordance with claim 1 , wherein the slag contains copper (Cu).
8. A method in accordance with claim 1 , wherein the slag contains lead (Pb), zinc (Zn), platinum (Pt), or nickel (Ni).