Process for preparing a diene elastomer, such as a polybutadiene
View Patent ↗The present invention relates to a process for preparing a diene elastomer. The invention especially applies to the production of a polybutadiene with a high level of cis-1,4 linkages that has at the same time a Mooney viscosity ML (1+4) greater than or equal to 40, a polydispersity index less than 2.1 and a reduced cold flow and of a polyisoprene. The process according to the invention comprises a reaction of a catalyst system with at least one conjugated diene monomer, this catalyst system being based on at least: one conjugated diene; one organic phosphoric acid salt of one or more rare-earth metals, said salt being in suspension and in at least one saturated and aliphatic or alicyclic, and inert hydrocarbon-based solvent; one alkylating agent composed of an alkyl aluminum for formula AlR 3 or HAlR 2 and a halogen donor belonging to the family of alkylaluminium halides, with the exclusion of alkylaluminium sesquihalides. This process comprises a separate bringing together of the monomer(s) to be polymerized with at least one alkylaluminium compound of formula AlR 3 or HAlR 2 which is identical or not to the alkylating agent of said catalyst system, said amount being chosen as a function of the characteristics of the polymerization medium and/or the polymerization conditions and/or said elastomer to be obtained.
1. Process for preparing a diene elastomer, comprising a continuous or batch polymerization reaction, in solution or in bulk, of at least one conjugated diene monomer with a catalyst system, said catalyst system being based on at least:
one preforming conjugated diene monomer;
one organic phosphoric acid salt of one or more rare-earth metals, said salt being in suspension and in at least one saturated, aliphatic or alicyclic, inert hydrocarbon-based solvent;
one alkylating agent composed of an alkyl aluminium of formula AlR 3 or HAlR 2 in which R represents an alkyl radical and H a hydrogen atom; and
a halogen donor belonging to the family of alkylaluminium halides, with the exclusion of alkylaluminium sesquihalides,
wherein at least one alkylaluminium compound of formula AlR 3 or HAlR 2 in which R represents an alkyl radical and H represents a hydrogen atom, which is identical or not to that of said catalyst system, is separately introduced at a time different from the time of introduction of the catalyst system, into an industrial polymerization unit; and
wherein the separately introduced alkylaluminium compound and the alkylating agent are present in a molar ratio that varies from 0.05 to 3.
2. Process according to claim 1 , wherein all of the separately introduced alkylaluminium compound(s) of formula AlR 3 or HAlR 2 wherein R and H have the same meanings as in claim 1 added is introduced into the industrial polymerization unit before the introduction of the catalyst system.
3. Process according to claim 1 wherein prior to the polymerization reaction, the separately introduced alkyaluminium compound of formula AlR 3 or HAlR 2 , wherein R and H have the same meanings as in claim 1 is brought together with the conjugated diene monomer(s) to be polymerized.
4. Process according to claim 1 wherein prior to the polymerization reaction, the separately introduced alkyaluminium compound of formula AlR 3 or HAlR 2 , wherein R and H having the same meanings as in claim 1 is brought together with the conjugated diene monomer(s) to be polymerized and the polymerization solvent.
5. Process according to claim 1 , wherein the alkylating agent/salt of rare-earth element(s) molar ratio in said catalyst system has a value ranging from 1 to 10.
6. Process according to claim 1 , wherein the amount of said separately introduced alkylaluminium compound brought together with said conjugated diene monomer(s) to be polymerized varies from 10 to 5,000 μmol per 100 g of conjugated diene monomer(s) to be polymerized.
7. Process according to claim 6 , wherein said separately introduced alkylaluminium compound is used in an amount ranging from 50 to 1,000 μmol per 100 g of conjugated diene monomer(s) to be polymerized, then said catalyst system is used in an alkylating agent/salt of rare-earth element(s) molar ratio ranging from 1 to 5.
8. Process according to claim 1 , wherein said reaction is carried out continuously, said separately introduced alkylaluminium compound being brought together with said conjugated diene monomers) to be polymerized in a line inlet located upstream of at least one polymerization reactor.
9. Process according to claim 8 , wherein said catalyst system is incorporated in its entirety in the industrial polymerization unit, in said line inlet.
10. Process according to claim 8 , wherein said catalyst system is incorporated in its entirety in the industrial polymerization unit directly in said reactor.
11. Process according to claim 1 , wherein said reaction is carried out in an inert hydrocarbon-based polymerization solvent or else in bulk.
12. Process according to claim 1 , wherein said separately introduced alkylaluminium compound is diisobutylaluminium hydride.
13. Process according to claim 1 , wherein said halogen donor is an alkylaluminium monohalide.
14. Process according to claim 1 , wherein said salt is a tris[bis(2-ethylhexyl)phosphate] of rare-earth element(s).
15. Process according to claim 1 , wherein said alkylating agent comprises diisobutylaluminium hydride.
16. Process according to claim 1 , wherein said catalyst system comprises said rare-earth metal or metals in a concentration greater than or equal to 0.002 mol/l.
17. Process according to claim 1 , wherein the halogen donor/salt molar ratio has a value ranging from 2 to 3.5.
18. Process according to claim 1 , wherein the preforming conjugated diene monomer/salt molar ratio has a value ranging from 15 to 70.
19. Process according to claim 1 , wherein said conjugated diene monomer to be polymerized is butadiene, in order to obtain a butadiene homopolymer having at the same time:
a Mooney viscosity ML(1+4) at 100° C., measured according to the standard
ASTM D 1646, which is greater than or equal to 40;
a polydispersity index less than 2.1;
a level of cis-1,4 linkages greater than 90%; and
a reduced cold flow ranging from 0.01 g to 0.5 g.
20. Process according to claim 1 , wherein said conjugated diene monomer to be polymerized is butadiene, in order to obtain a butadiene homopolymer having a cold flow ranging from 0.01 g to 0.3 g.
21. Process according to claim 1 , wherein the conjugated diene monomer to be polymerized is isoprene in order to obtain a polyisoprene.