Synergistic organoborate compositions and lubricating compositions containing same
View Patent ↗An additive for imparting antiwear properties to a lubricant composition is based on a combination of (1) an organo borate ester composition and (2) one or more sulfur- or phosphorus-containing compounds or a non-sulfur molybdenum compound. The sulfur- or phosphorus-containing compounds are dithiocarbamate, bisdithiocarbamate, 1,3,4-diathiazole, phosphorodithioate, phosphorodithioate esters, and the molybdenum compound is prepared by reacting (a) about 1.0 mole of fatty oil having 12 or more carbon atoms, (b) about 1.0 to 2.5 moles diethanolamine and (c) a molybdenum source.
1. A lubricating composition comprising:
a) a major portion of an oil of lubricating viscosity; and
b) about 0.1 to 10% by mass of an antiwear additive comprising:
1) an organo borate ester composition formed by reacting about 1 mole fatty oil and about 1.8 moles diethanolamine, followed by subsequent reaction with boric acid, wherein the boron content of the organo borate ester composition is between about 0.6 and about 2.7% wt %, and wherein the amount of organo borate ester in the lubricating composition is less than about 1.0% by weight; and
2) an alkyl zinc dithiophosphate wherein the ratio of organo borate ester composition:alkyl zinc dithophosphate is from 1:15 to 15:1.
2. The lubricating composition according to claim 1 wherein component (2) comprises a primary zinc dithiophosphate.
3. The lubricating composition according to claim 2 wherein the ratio is about 1:9 to 9:1.
4. The lubricating composition of claim 1 , wherein the boron content of the organo borate ester composition is between about 0.8 and about 1.2 wt %.
5. The lubricating composition of claim 1 , wherein the alkyl zinc dithiophosphate comprises primary and/or secondary alkyl zinc dithiophosphate.
6. The lubricating composition of claim 5 , wherein the boron content of the organo borate ester composition is between about 0.8 and about 1.2 wt %.
7. The lubricating composition of claim 1 , wherein the boron content of the lubricating composition is between about 15 to 50 ppm.
8. The lubricating composition according to claim 7 , wherein component (2) comprises a primary zinc dithiophosphate.