Method for forming porous PTFE layer
A method forming a porous PTFE layer includes steps of: combining one or at least two unburned porous PTFE films and a support body that can withstand a heating condition in the following process (a rod or plate shaped support body made of mesh or the like is preferable) by using a predetermined means in such a manner that a slip can be prevented in a heating treatment in the following process; and heating the matter resulted from the above process at a temperature of at least 150° C. and less than the melting point of the PTFE film for the range of 5-120 minutes (preferably at a temperature in the range of the melting point of a thermoplastic resin fiber to 320° C. for the range of 10-60 minutes in the case in which the thermoplastic resin fiber or the like is used in the process.
1. A method for forming a porous PTFE layer, comprising the steps of:
(1) combining one or at least two unburned porous polytetrafluoroethylene (PTFE) films and a plate shaped support body that can withstand a heating condition in the following process ( 2 ) by disposing the PTFE film on one face of the plate shaped support body and bending a peripheral section having a width of at least 1 cm in the PTFE film to the rear side of the support body; and
(2) heating the matter resulted from the above process ( 1 ) at a temperature of at least 150° C. and less than the melting point of the PTFE film for the range of 5 to 120 minutes.
2. The method for forming a porous PTFE layer as defined in claim 1 , wherein the at least two unburned porous PTFE films are sewn to each other by using a thermoplastic resin fiber in advance, and the heating treatment in the process ( 2 ) is carried out at a temperature in the range of the melting point of the used resin fiber to 320° C. for the range of 10 to 60 minutes.
3. The method for forming a porous PTFE layer as defined in claim 2 , wherein the fiber is a fiber made of ethylene tetrafluoroethylene hexafluoropropylene copolymer (EFEP), tetrafluoroethylene hexafluoropropylene copolymer (FEP), or tetrafluoroethylene perfluoro alkoxyethylene copolymer (PFA), and the heating treatment in the process ( 2 ) is carried out at a temperature in the range of 200 to 320° C. for the range of 10 to 60 minutes.
4. The method for forming a porous PTFE layer as defined in any one of claim 2 , wherein the plate shaped support body is made of a mesh, a non-woven fiber, a braided rope, or a woven fabric.