Pigment dispersion
View Patent ↗The invention relates to a method of producing a substantially aqueous pigment dispersion substantially free from an organic binder comprising mixing at least one water-soluble or water-dispersible silane compound and colloidal silica particles to form silanized colloidal silica particles in an aqueous dispersion whereby said at least one silane compound is mixed with colloidal silica particles in a weight ratio of silane to silica of from about 0.2 to about 1.5, mixing said silanized colloidal silica particles with an organic and/or inorganic pigment, wherein the weight ratio of silica to pigment is from about 0.001 to about 0.8 to form said substantially aqueous pigment dispersion. The invention also relates to an aqueous pigment dispersion obtained from the method defined herein.
1. A method of producing a substantially aqueous pigment dispersion having an organic binder content less than 0.1 wt % and a total pigment content ranging from about 25 to about 85 wt %, said method comprising mixing at least one water-soluble or water-dispersible silane compound and colloidal silica particles having an average particle size in the range of about 2 to about 100 nm to form silanized colloidal silica particles in an aqueous dispersion whereby said at least one silane compound is mixed with said colloidal silica particles in a weight ratio of silane to silica of from about 0.2 to about 1.5, mixing said silanized colloidal silica particles with an organic and/or inorganic pigment, wherein the weight ratio of silica to pigment is from about 0.02 to about 0.4 to form said substantially aqueous pigment dispersion.
2. The method according to claim 1 , wherein the pigment has a particle size ranging from about 10 to about 5000 nm.
3. The method according to claim 1 , wherein the pigment is TiO 2 .
4. The method according to claim 1 , wherein the weight ratio of silane to silica is from about 0.25 to about 1.5.
5. The method according to claim 1 , wherein the aqueous pigment dispersion contains up to about 20% by volume of a water-soluble or water-dispersible organic solvent.
6. The method according to claim 1 , wherein the weight ratio of silica to pigment is from about 0.01 to about 0.2.
7. An aqueous pigment dispersion having an organic binder content less than 0.1 wt % and a total pigment content ranging from about 25 to about 85 wt %, said pigment dispersion obtained by mixing at least one water-soluble or water-dispersible silane compound and colloidal silica particles having an average particle size in the range of about 2 to about 100 nm to form silanized colloidal silica particles in an aqueous dispersion whereby said at least one silane compound is mixed with said colloidal silica particles in a weight ratio of silane to silica of from about 0.2 to about 1.5, mixing said silanized colloidal silica particles with an organic and/or inorganic pigment, wherein the weight ratio of silica to pigment is from about 0.02 to about 0.4 to form said substantially aqueous pigment dispersion.
8. The dispersion according to claim 7 , wherein the weight ratio of silica to pigment is from about 0.01 to about 0.2.
9. An aqueous pigment dispersion having an organic binder content less than 0.1 wt % and a total silica content ranging from about 1 to about 80 wt % comprising silanized colloidal silica particles having an average particle size in the range of about 2 to about 100 nm, wherein the weight ratio of silane to silica in the pigment dispersion is from about 0.2 to about 1.5; and an organic and/or inorganic pigment, wherein the weight ratio of silica to pigment is from about 0.02 to about 0.4.
10. The dispersion according to claim 9 , wherein the pigment has a particle size ranging from about 10 to about 5000 nm.
11. The dispersion according to claim 9 , wherein the weight ratio of silane to silica is from about 0.25 to about 1.5.
12. The dispersion according to claim 9 , wherein the pigment content in the dispersion is from about 25 to about 85 wt %.
13. The dispersion according to claim 9 , wherein the pigment is inorganic.
14. The dispersion according to claim 9 , wherein the pigment is TiO 2 .
15. The dispersion according to claim 9 , wherein the weight ratio of silica to pigment is from about 0.01 to about 0.2.