Method for making anodes for electrolytic capacitor with high volumetric efficiency
View Patent ↗A method for manufacturing valve metal anodes of electrolytic capacitors by deoxidizing the anodes using Mg vapor in a deoxidizing furnace, removing the anodes from deoxidizing furnace, placing them in sintering furnace, sintering at temperature lower than the temperature conventionally used for sintering in vacuum, and leaching of Mg oxide off the anode surface. The process limits free oxygen and improves morphology of valve metal anodes, which results in improved performance of electrolytic capacitors with these anodes. The process does not require any special equipment or maintenance operations and, thereby, is highly productive due to performing deoxidizing and sintering separately in traditional deoxidizing and sintering furnaces.
1. A process of manufacturing valve metal anodes for electrolytic capacitors with high volumetric efficiency comprising: pressing of pellets from a valve metal powder, deoxidizing of pressed pellets with reducing agent in a deoxidizing furnace to form an anode; forming a sealing layer on all anode surfaces preventing oxidation; removing said anode from said deoxidizing furnace; placing said anode in a sintering furnace; sintering in a vacuum or under inert gas; and leaching of the sealing layer from the anode surfaces.
2. A process according to claim 1 wherein reducing agent is Mg and deoxidizing temperatures are about the range 700° C.-1100° C.
3. A process according to claim 1 wherein said sealing layer is MgO.
4. A process according to claim 1 , wherein the sintering temperature is above deoxidizing temperature and below the temperature conventionally used for sintering in vacuum.
5. A process according to claim 1 , wherein leaching of sealing layer is performed in water solution of sulfuric acid and hydrogen peroxide.
6. A process according to claim 1 wherein a lead wire has been pressed with the anode pellets.
7. A process according to claim 1 wherein an anode lead is attached after pressing or sintering.