Hyperelastic shape setting devices and fabrication methods
View Patent ↗Shape-setting methods for fabricating devices made of single crystal shape memory alloys. The method include drawing a single crystal of a shape memory alloy from a melt of the alloy. This is followed by heating and quenching the crystal sufficiently rapid to limit the formation of alloy precipitates to an amount which retains hyperelastic composition and properties of the crystal.
1. A method of shape-setting a device so that it is comprised of a single crystal shape memory alloy, the method comprising the steps of heating the device to a first temperature sufficient for annealing the alloy, forming the device into a shape, constraining the device while in the shape, heating the device to a second temperature and within a first time period with the second temperature and first time period being sufficient to cause the alloy to lose its strength, and cooling the device to a third temperature and within a second time period with the third temperature and second time period being sufficient to cause the alloy to form a single crystal.
2. A method as in claim 1 in which the forming step is carried out by forming the shape of device into a wire shape, providing a tube which generally conforms to the shape of the wire, and inserting the wire into the tube.
3. A method as in claim 2 in which the step of providing a tube comprises providing a tube of stainless steel.
4. A method of shape-setting a device so that it is comprised of a single crystal shape memory alloy, the method comprising the steps of:
heating the device to an annealing temperature sufficient for annealing the alloy, wherein the device comprises a single crystal shape memory alloy;
forming the device into a shape;
constraining the device while in the shape and holding the device in the shape for a first time period sufficient to cause the alloy to lose its strength; and
cooling the device to a cooling temperature for a second time period, wherein the cooling temperature and second time period are sufficient to cause the alloy to remain a single crystal in the shape.
5. A method of shape-setting a device so that it is comprised of a single crystal shape memory alloy of CuAlNi, the method comprising the steps of:
heating the device to a first temperature sufficient for placing the Cu, Al and Ni in solution;
rapidly quenching the device to a second temperature to prevent precipitation of the Cu, Al and Ni so that the device remains as a single crystal of CuAlNi;
forming the device into a shape;
constraining the device while in the shape;
heating the device to a third temperature for a first time period, wherein the third temperature and first time period are sufficient to cause the alloy to lose its strength; and
cooling the device to a fourth temperature for a second time period, wherein the fourth temperature and second time period are sufficient to cause the alloy to remain a single crystal in the shape.