Methacrylate resin with excellent discoloration-resistance and transparency and method for preparing the same
One aspect of the invention relates to a methacrylate resin prepared by suspension polymerization using a polyalkylacrylate-acrylic acid as a suspension stabilizer. The suspension stabilizer is used in an amount of about 0.05 to about 0.25 parts by weight per 100 parts by weight of a monomer mixture. Another aspect of the invention relates to a method for preparing a methacrylate resin, which comprises: preparing a mixture by mixing an initiator and a chain-transfer agent with a monomer mixture comprising at least about 50% by weight of alkyl methacrylate; and adding the mixture to an aqueous solution of polyalkylacrylate-acrylic acid to conduct suspension polymerization.
1. A methacrylate resin prepared by suspension polymerization wherein a polyalkylacrylate-acrylic acid selected from the group consisting of is used as a suspension stabilizer, wherein said suspension stabilizer is used in an amount of about 0.05 to about 0.25 parts by weight per 100 parts by weight of a monomer mixture used to prepare of the said methacrylate resin.
2. The methacrylate resin of claim 1 , wherein said monomer mixture comprises about 50 to about 100% by weight of an alkyl methacrylate, and about 0 to about 50% by weight of a monomer copolymerizable with the alkyl methacrylate.
3. The methacrylate resin of claim 2 , wherein the monomer copolymerizable with the alkyl methacrylate comprises a monomer selected from the group consisting of methacrylic acid ester monomers; acrylic acid ester monomers; unsaturated carboxylic acid monomers; acid anhydride monomers; hydroxyl group containing ester monomers; amide monomers; nitrile monomers; allyl glycidyl ethers; glycidyl methacrylates; styrenic monomers; and combinations thereof.
4. The methacrylate resin of claim 3 , wherein said methacrylic acid ester monomer comprises a monomer selected from the group consisting of ethyl methacrylate, propyl methacrylate, butyl methacrylate, and benzyl methacrylate; said acrylic acid ester monomer comprises a monomer selected from the group consisting of methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, and 2-ethyl hexyl acrylate; said unsaturated carboxylic acid monomer comprises a monomer selected from the group consisting of acrylic acid and methacrylic acid; said acid anhydride monomer comprises maleic anhydride; said hydroxyl group containing ester monomer comprises a monomer selected from the group consisting of 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, and monoglycerol acrylate; said amide monomer comprises a monomer selected from the group consisting of acryl amide and methacryl amide; said nitrile monomer comprises a monomer selected from the group consisting of acrylonitrile and methacrylonitrile; and said styrenic monomer comprises a monomer selected from the group consisting of styrene and α-methyl styrene.
5. The methacrylate resin of claim 2 , wherein said alkyl methacrylate is methyl methacrylate, ethyl methacrylate, propyl methacrylate, or butyl methacrylate.
6. The methacrylate resin of claim 1 , wherein said methacrylate resin has a weight average molecular weight of from about 15,000 to about 200,000.
7. The methacrylate resin of claim 1 , wherein said methacrylate resin has a Yellow Index according to ASTM D-1925 of about 0.9 or less, a total light transmittance at a sample thickness of 3.0 mm of about 92% or more and a haze of about 0.6 or less.
8. A method for preparing a methacrylate resin of claim 1 , comprising:
preparing a mixture by mixing an initiator and a chain-transfer agent with a monomer mixture comprising at least about 50% by weight of alkyl methacrylate; and
adding the mixture to an aqueous solution of polyalkylacrylate-acrylic acid selected from the group consisting of polyethylacrylate-acrylic acid and polyethyl-hexylacrylate-acrylic acid under conditions to conduct suspension polymerization.
9. The method of claim 8 , wherein said aqueous solution of polyalkylacrylate-acrylic acid further comprises a suspension stabilization aid.
10. The method of claim 8 , wherein said polymerization is conducted at about 70 to about 120° C. for about 2 to about 8 hours.
11. The method of claim 8 , wherein said polymerization is conducted in the presence of additives selected from the group consisting of lubricants, ultraviolet absorbents, dyes, antioxidants, and combinations thereof.
12. The methacrylate resin of claim 1 , wherein said methacrylate resin has a Yellow Index according to ASTM D-1925 of about 0.1 to about 0.85, a total light transmittance at a sample thickness of 3.0 mm of about 93 to about 99% and a haze of about 0.1 to about 0.55.
13. The method of claim 8 , wherein said suspension polymerization is initiated after the mixture of initiator, chain-transfer agent and monomer mixture is added to the aqueous solution of polyalkylacrylate-acrylic acid.
14. The method of claim 8 , wherein said suspension stabilizer is used in an amount of about 0.05 to about 0.25 parts by weight per 100 parts by weight of said monomer mixture.