Silicate-based yellow-green phosphors
View Patent ↗Novel phosphor systems are disclosed having the formula A 2 SiO 4 :Eu 2+ D, where A is at least one of a divalent metal selected from the group consisting of Sr, Ca, Ba, Mg, Zn, and Cd; and D is a dopant selected from the group consisting of F, Cl, Br, I, P, S, N, and B. In one embodiment, the novel phosphor has the formula (Sr 1−x−y Ba x M y ) 2 SiO 4 :Eu 2+ F (where M is one of Ca, Mg, Zn, or Cd in an amount ranging from 0<y<0.5). The phosphor is configured to absorb visible light from a blue LED, and luminescent light from the phosphor plus light from the blue LED may be combined to form white light. The novel phosphors can emit light at intensities greater than either conventionally known YAG compounds, or silicate-based phosphors that do not contain the inventive dopant ion.
1. A white LED comprising:
a radiation source configured to emit radiation having a wavelength ranging from about 410 to 500 nm;
a green phosphor having the formula (Sr 1−x−y Ba x M y ) 2 SiO 4 :Eu 2+ F,Cl,Br,I,S,N,B, where M is at least one of an element selected from the group consisting of Ca, Mg, Zn, and Cd; where F, Cl, Br, I, S, N, B are used in any combination having a total molar dopant level in the range 0.0001-0.2; and where
0.3≦x≦1;
0≦y≦0.5 when M is Ca;
0≦y≦0.1 when M is Mg; and
0≦y≦0.5 when M is selected from the group consisting of Zn and Cd, the green phosphor configured to absorb at least a portion of the radiation from the radiation source and emit light with peak intensity in a wavelength ranging from about 500 to 540 nm;
a red phosphor selected from the group consisting of
CaS:Eu 2+ ;
SrS:Eu 2+ ;
MgO*MgF*GeO:Mn 4+ ;
a nitridosilicate, an aluminonitridosilicate, an oxynitridosilicate, and an oxynitridoaluminosilicate;
M x Si y N z :Eu 2+ where M is selected from the group consisting of Ca, Sr, Ba, and Zn; and Z=⅔x+ 4/3y;
M 2 Si 5 N 8 :Eu 2+ , where M is Ca, Sr, and Ba;
CaSiN 2 :Eu 2+ ;
CaAlSiN 3 :Eu 2+ ;
(Ca 1−x−y−z Sr x Ba y Mg z ) 1−n (Al 1−a+b B a )Si 1−b N 3−b O b :RE n , where 0≦x≦1, 0≦y≦1, 0≦z≦1, 0≦a≦1, 0<b≦1, 0.002≦n≦0.2, and RE is selected from the group consisting of Eu 2+ and Ce 3+ ; and
wherein the red phosphor is configured to absorb at least a portion of the radiation from the radiation source and emit light with peak intensity in a wavelength ranging from about 590 to 690 nm.
2. A white LED comprising:
a radiation source configured to emit radiation having a wavelength ranging from about 410 to 500 nm;
a yellow phosphor having the formula (Sr 1−x−y Ba x M y ) 2 SiO 4 :Eu 2+ F,Cl,Br,I,S,N,B, where M is at least one of an element selected from the group consisting of Ca, Mg, Zn, Cd; where F, Cl, Br, I, S, N, B are used in any combination having a total molar dopant level in the range 0.0001-0.2; and where
0.3≦x≦1;
0≦y≦0.5 when M is Ca;
0≦y≦0.1 when M is Mg; and
0≦y≦0.5 when M is selected from the group consisting of Zn and Cd, the yellow phosphor configured to absorb at least a portion of the radiation from the radiation source and emit light with a peak intensity in a wavelength ranging from about 540 to 590 nm
a red phosphor selected from the group consisting of
CaS:Eu 2+ ;
SrS:Eu 2+ ;
MgO*MgF*GeO:Mn 4+ ;
a nitridosilicate, an aluminonitridosilicate, an oxynitridosilicate, and an oxynitridoaluminosilicate;
M x Si y N z :Eu 2+ where M is selected from the group consisting of Ca, Sr, Ba, and Zn; and Z=⅔x+ 4/3y;
M 2 Si 5 N 8 :Eu 2+ , where M is Ca, Sr, and Ba;
CaSiN 2 :Eu 2+ ;
CaAlSiN 3 :Eu 2+ ;
(Ca 1−x−y−z Sr x Ba y Mg z ) 1−n (Al 1−a+b B a )Si 1−b N 3−b O b :RE n , where 0≦x≦1, 0≦y≦1, 0≦z≦1, 0≦a≦1, 0<b≦1, 0.002≦n≦0.2, and RE is selected from the group consisting of Eu 2+ and Ce 3+ ; and
wherein the red phosphor is configured to absorb at least a portion of the radiation from the radiation source and emit light with peak intensity in a wavelength ranging from about 590 to 690 nm.