Semi-batch process for producing fluoroelastomers
View Patent ↗A novel semi-batch emulsion polymerization process for the production of fluoroelastomers is disclosed wherein a hydrocarbon anionic surfactant is employed as the dispersing agent. The surfactant has the formula R-L-M wherein R is an alkyl group having between 6 and 17 carbon atoms, L is selected from the group consisting of ArSO 3 − , SO 3 − , SO 4 − , PO 3 − and COO − and M is a univalent cation. Preferred surfactants are sulfonates of the formula CH 3 —(CH 2 ) n —SO 3 M, CH 3 —(CH 2 ) n —C 6 H 4 —SO 3 M, or CH 3 —(CH 2 ) n —CH═CHCH 2 —SO 3 M, where n is an integer from 6 to 17, or mixtures thereof, and M is a cation having a valence of 1. Surfactant is not introduced to the reactor until shortly after the polymerization reaction has begun.
1. A semi-batch emulsion polymerization process for the production of a fluoroelastomer, said fluoroelastomer having at least 58 weight percent fluorine, comprising:
(A) charging a reactor with a quantity of an aqueous solution substantially free of surfactant;
(B) charging said reactor with a quantity of a monomer mixture comprising i) from 25 to 75 weight percent, based on total weight of the monomer mixture, of a first monomer, said first monomer selected from the group consisting of vinylidene fluoride and tetrafluoroethylene, and ii) between 75 and 25 weight percent, based on total weight of said monomer mixture, of one or more additional copolymerizable monomers, different from said first monomer, wherein said additional monomer is selected from the group consisting of fluorine-containing olefins, fluorine-containing vinyl ethers, hydrocarbon olefins and mixtures thereof;
(C) initiating polymerization to form a fluoroelastomer dispersion while maintaining said reaction medium at a pH between 1 and 7, at a pressure between 0.5 and 10 MPa, and at a temperature between 25° C. and 130° C.; and
(D) charging said reactor, after polymerization has begun, with a quantity of a hydrocarbon anionic surfactant of the formula R-L-M wherein R is an alkyl group having between 6 and 17 carbon atoms, L is selected from the group consisting of —ArSO 3 − , —SO 3 − , —SO 4 − , —PO 3 − and —COO − and M is a univalent cation.
2. The semi-batch emulsion polymerization process of claim 1 further comprising (E) isolating fluoroelastomer from said dispersion by addition of a coagulating agent.
3. The semi-batch emulsion polymerization process of claim 1 wherein said surfactant is selected from the group consisting of CH 3 —(CH 2 ) n —SO 3 M, CH 3 —(CH 2 ) n —C 6 H 4 —SO 3 M, CH 3 —(CH 2 ) n —CH═CHCH 2 —SO 3 M, CH 3 —(CH 2 ) n —SO 4 M, CH 3 —(CH 2 ) n —PO 3 M, and CH 3 —(CH 2 ) n —COOM, wherein n is an integer from 6 to 17.
4. The semi-batch emulsion polymerization process of claim 3 wherein said surfactant is CH 3 —(CH 2 ) n —SO 3 M, wherein n is an integer from 7 to 14.
5. The semi-batch emulsion polymerization process of claim 1 further comprising charging said reactor with a chain transfer agent.
6. The semi-batch emulsion polymerization process of claim 1 wherein said monomer mixture further comprises 0.05 to 10 weight percent, based on total weight of the monomer mixture, of a cure site monomer.
7. The semi-batch emulsion polymerization process of claim 1 wherein said fluoroelastomer comprises copolymerized monomer units selected from the group consisting of i) vinylidene fluoride and hexafluoropropylene; ii) vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene; iii) vinylidene fluoride, hexafluoropropylene, tetrafluoroethylene and 4-bromo-3,3,4,4-tetrafluorobutene-1; iv) vinylidene fluoride, hexafluoropropylene, tetrafluoroethylene and 4-iodo-3,3,4,4-tetrafluorobutene-1; v) vinylidene fluoride, perfluoro(methyl vinyl) ether, tetrafluoroethylene and 4-bromo-3,3,4,4-tetrafluorobutene-1; vi) vinylidene fluoride, perfluoro(methyl vinyl) ether, tetrafluoroethylene and 4-iodo-3,3,4,4-tetrafluorobutene-1; vii) vinylidene fluoride, perfluoro(methyl vinyl) ether, tetrafluoroethylene and 1,1,3,3,3-pentafluoropropene; viii) tetrafluoroethylene, perfluoro(methyl vinyl) ether and ethylene; ix) tetrafluoroethylene, perfluoro(methyl vinyl) ether, ethylene and 4-bromo-3,3,4,4-tetrafluorobutene-1; x) tetrafluoroethylene, perfluoro(methyl vinyl) ether, ethylene and 4-iodo-3,3,4,4-tetrafluorobutene-1; xi) tetrafluoroethylene, propylene and vinylidene fluoride; xii) tetrafluoroethylene and perfluoro(methyl vinyl) ether; xiii) tetrafluoroethylene, perfluoro(methyl vinyl) ether and perfluoro(8-cyano-5-methyl-3,6-dioxa-1-octene); xiv) tetrafluoroethylene, perfluoro(methyl vinyl) ether and 4-bromo-3,3,4,4-tetrafluorobutene-1; xv) tetrafluoroethylene, perfluoro(methyl vinyl) ether and 4-iodo-3,3,4,4-tetrafluorobutene-1; and xvi) tetrafluoroethylene, perfluoro(methyl vinyl) ether and perfluoro(2-phenoxypropyl vinyl) ether.