Time release calcium sulfate and growth factor matrix for bone augmentation
A bone-growth stimulating composition for forming a resorbable implant, methods for making such a composition and a corresponding putty/paste material. In some embodiments of the invention, such a material includes a plurality of particles having a predetermined size and comprising a first calcium sulfate compound, a resorbable polymer in a predetermined weight ratio and a growth factor.
1 . A bone-growth stimulating particle, a plurality of which for use together for forming a resorbable implant, having a size between about 425 μm and about 850 μm in diameter and comprising a calcium sulfate compound, a resorbable polymer in a weight ratio of about 96:4, and a growth factor.
2 . The particle according to claim 1 , wherein the growth factor is selected from the group consisting of: bone morphogenetic proteins, platelet derived growth factor, transforming growth factor, fibroblast growth factor, vascular endothelial growth factor, brain derived neurotrophic factor, insulin-like growth factor, epidermal growth factor, and combinations thereof.
3 . The particle according to claim 1 , wherein the calcium compound of the particle and growth factor is substantially encapsulated by the resorbable polymer according to a predetermined thickness.
4 . The particle according to claim 3 , wherein the encapsulation includes one or more imperfections.
5 . The particle according to claim 2 , wherein the thickness of the coating is between about 2 μm and about 50 μm.
6 . The bone-growth stimulating composition according to claim 1 , wherein the calcium sulfate compound comprises calcium sulfate hemihydrate.
7 . The bone-growth stimulating composition according to claim 1 , wherein the resorbable polymer is selected from the group consisting of: aliphatic polyesters of alpha-hydroxy acid derivatives, such as polyactides, polyglycolides, polydioxanone, polyepsilon.-caprolactone; hydrophobic polymers, such as carnuba waxes and their derivatives; water soluble polymers, such as poly(desaminotyrosyl-tyrosine ethyl ester carbonate) (“DTE carbonate”) and their derivatives; and therapeutic polymers, such as those containing salicylate, and combinations thereof.
8 . A bone-growth stimulating composition for forming a resorbable implant comprising:
a plurality of particles having a size between about 425 μm and about 850 μm in diameter and comprising a first calcium sulfate compound, a resorbable polymer in a weight ratio of about 96:4, and a growth factor.
9 . The bone-growth stimulating composition according to claim 8 , wherein the growth factor is selected from the group consisting of: bone morphogenetic proteins, platelet derived growth factor, transforming growth factor, fibroblast growth factor, vascular endothelial growth factor, brain derived neurotrophic factor, insulin-like growth factor, epidermal growth factor, and combinations thereof.
10 . The bone-growth stimulating composition according to claim 8 , wherein the resorbable polymer comprises a coating covering at least a portion of the calcium/growth factor compound according to a predetermined thickness.
11 . The bone-growth stimulating composition according to claim 8 , wherein the calcium/growth factor compound of a particle is substantially encapsulated by the resorbable polymer according to a predetermined thickness.
12 . The bone-growth stimulating composition according to claim 11 , wherein the encapsulation includes one or more imperfections.
13 . The bone-growth stimulating composition according to claim 10 , wherein the thickness of the coating is between about 2 μm and about 50 μm.
14 . The bone-growth stimulating composition according to claim 8 , wherein the calcium sulfate compound comprises calcium sulfate hemihydrate.
15 . The bone-growth stimulating composition according to claim 8 , wherein the resorbable polymer is selected from the group consisting of: aliphatic polyesters of alpha-hydroxy acid derivatives, such as polyactides, polyglycolides, polydioxanone, polyepsilon.-caprolactone; hydrophobic polymers, such as carnuba waxes and their derivatives; water soluble polymers, such as poly(desaminotyrosyl-tyrosine ethyl ester carbonate) (“DTE carbonate”) and their derivatives; and therapeutic polymers, such as those containing salicylate, and combinations thereof.
16 . A bone-growth stimulating putty for forming a resorbable implant comprising:
a plurality of polymer containing particles having a size between about 425 μm and about 850 μm in diameter and comprising a calcium sulfate compound, a resorbable polymer;
a growth factor; and
a plasticizer/thickener.
17 . The bone growth stimulating putty according to claim 16 , wherein the plasticizer/thickener is selected from the group consisting of: carboxymethylcellulose, hydroxymethylcellulose, hydroxyethylcellulose, hydroxypropyl methylcellulose, hydroxyethylcellulose polyvinyl alcohol, polyvinyl pyrrolidone, hyaluronate and chitin derivatives such as chitosan and combinations thereof.
18 . The bone growth stimulating putty according to claim 16 , wherein a weight ratio of calcium sulfate to resorbable polymer in the plurality of polymer containing particles is about 96:4.
19 . The bone-growth stimulating putty according to claim 16 , wherein a weight ratio of the polymer containing particles to plasticizer/thickener is between about 65:35 to 90:10.
20 . The bone-growth stimulating putty according to claim 16 , further comprising a separate calcium sulfate powder.
21 . The bone-growth stimulating putty according to claim 16 , wherein the growth factor is selected from the group consisting of: bone morphogenetic proteins, platelet derived growth factor, transforming growth factor, fibroblast growth factor, vascular endothelial growth factor, brain derived neurotrophic factor, insulin-like growth factor, epidermal growth factor, and combinations thereof.
22 . A method of delivering a growth factor to a target tissue over a period of time comprising:
providing a bone-growth stimulating composition, the composition comprising a plurality of particles having a predetermined diameter, wherein the particles comprise a first calcium sulfate compound, a growth factor and a resorbable polymer;
forming a resorbable implant and/or a resorbable bone putty from said composition;
implanting the implant and/or applying the bone putty to the target tissue, wherein the growth factor is released to the target tissue substantially continuously and/or consistantly over a period of time based upon the time-release properties of the composition.
23 . A method for manufacturing particles for use in forming a resorbable implant for stimulating bone growth, the method comprising:
rotating calcium sulfate powder in a drum at a first predetermined drum speed;
mixing in a growth factor;
a first spraying of a resorbable polymer solution at a first predetermined rate on the calcium sulfate powder over a first predetermined period of time; and
drying the resulting particles.