Process for producing vinyl polymer, vinyl polymer, and curable composition
View Patent ↗The present invention provides: a process for preparing a vinyl polymer containing a halogen in an amount of 1,000 mg or less per kilogram, in which a vinyl polymer containing the halogen produced by atom transfer radical polymerization of a vinyl monomer is heated at a temperature in the range of 140 to 250° C. to dehalogenate the vinyl polymer; a vinyl polymer obtained by the process; and a hydrosilylation-reactive curable composition containing the vinyl polymer.
1. A vinyl polymer prepared by a process for preparing a vinyl polymer containing halogen atoms in an amount of 1,000 mg or less per kilogram, the process comprising (a) producing a vinyl polymer containing halogen by atom transfer radical polymerization of a vinyl monomer; and (b) dehalogenating the vinyl polymer containing the halogen by heating the vinyl polymer containing the halogen at a temperature in the range of 140 to 250° C., wherein the dehalogenation step is performed by promoting an intramolecular cyclization reaction of the vinyl polymer containing the halogen produced by the atom transfer radical polymerization of the vinyl monomer, and the intramolecular cyclization reaction forms a lactone ring.
2. The vinyl polymer according to claim 1 , wherein the vinyl polymer has a number average molecular weight in the range of 1,000 to 100,000.
3. The vinyl polymer according to claim 1 , wherein the molecular weight distribution (weight average molecular weight/number average molecular weight) of the vinyl polymer is in the range of 1.05 to 1.50.
4. The vinyl polymer according to claim 1 , wherein the vinyl polymer has an ethylenically unsaturated group in the molecule thereof.
5. A hydrosilylation-reactive curable composition containing the vinyl polymer as set forth in claim 1 .
6. A vinyl polymer having a silyl group in the molecule thereof, the vinyl polymer being prepared by allowing the ethylenically unsaturated group of the vinyl polymer as set forth in claim 4 to react with a compound containing a hydrosilyl group.
7. The vinyl polymer having a silyl group in the molecule thereof according to claim 6 , wherein the vinyl polymer has a number average molecular weight in the range of 1,000 to 100,000.
8. The vinyl polymer having a silyl group in the molecule thereof according to claim 6 , wherein the molecular weight distribution (weight average molecular weight/number average molecular weight) of the vinyl polymer is in the range of 1.05 to 1.50.
9. A curable composition containing the vinyl polymer having a silyl group in the molecule thereof as set forth in claim 6 .