Surface-modified nanoparticles from aluminum oxide and oxides of the elements of the first and second main group of the periodic system, and the production thereof
The invention relates to mixed oxide nanoparticles from aluminum oxide or oxides of the elements of the first and second main group of the periodic system. These mixed oxide nanoparticles are surface-modified with a coating agent, preferably a silane or siloxane.
1 . A surface modified nanoparticle comprising 50-99.9% by weight of aluminum oxide predominantly in the rhombohedral α modification and 0.1-50% by weight of at least one oxide of at least one element of main groups I and II of the Periodic Table, wherein the surface of the nanoparticle is modified by a coating agent.
2 . A surface modified nanoparticle as claimed in claim 1 , wherein the coating agent is a siloxane or silane.
3 . A surface modified nanoparticle as claimed in claim 1 , wherein the mixed oxides have a crystallite size of less than 1 μm.
4 . A process for producing the surface modified nanoparticle as claimed in claim 1 , comprising the steps of deagglomerating the agglomerates of the nanoparticles in the presence of an organic solvent by milling and simultaneously or subsequently treating the nanoparticle with a coating agent.
5 . The process as claimed in claim 4 , wherein the deagglomerating step is performed by milling in a stirred ball mill.
6 . The process as claimed in claim 4 , wherein the deagglomerating step is performed by milling at from 20 to
7 . The process as claimed in claim 4 , wherein the deagglomerating step is carried out in a C 1 -C 4 -alcohol as solvent.
8 . The process as claimed in claim 4 , wherein the deagglomerating step is carried out in acetone, tetrahydrofuran, butyl acetate or other solvents used in the surface coatings industry.
9 . The process as claimed in claim 4 , wherein the molar ratio of nanoparticles to coating agent is from 1:1 to 10:1.
10 . A surface-modified nanoparticle as claimed in claim 1 , wherein the mixed oxides have a crystallite size of less than 0.2 μm.
11 . A surface-modified nanoparticle as claimed in claim 1 , wherein the mixed oxides have a crystallite size in the range from 0.001 μm to 0.1 μm.
12 . A process as claimed in claim 4 , wherein the coating agent is a silane, a siloxane or mixture thereof.