Aluminium oxide dispersion
View Patent ↗Aluminum oxide dispersion, which is stable in a pH range 5 from 5 to 9 and has an aluminum oxide content of at least 40 wt. %, obtainable by dispersing pyrogenically produced aluminum oxide particles in an aqueous phase, wherein one or several at least dibasic hydroxycarboxylic acids present dissolved in the dispersion and at least one salt of a 10 dialkali metal hydrogen phosphate and/or alkali metal dihydrogen phosphate are added to the aqueous phase each mutually independently in a quantity of 0.3−3×10 −6 mol/m2 of aluminum oxide specific surface area.
1. An aluminum oxide dispersion, which is stable in a pH range from 5 to 9 and has an aluminum oxide content of at least 40 wt. %, obtainable by dispersing one or several aluminum oxide powders with a specific surface area of 5 to 200 m 2 /g in an aqueous phase, wherein one or several at least dibasic hydroxycarboxylic acids present dissolved in the dispersion and at least one salt of a dialkali metal hydrogen phosphate and/or alkali metal dihydrogen phosphate are added to the aqueous phase each mutually independently in a quantity of 0.3-3×10 −6 mol/m 2 of aluminum oxide specific surface area.
2. The aluminum oxide dispersion according to claim 1 , wherein the aluminum oxide powder is of pyrogenic origin.
3. The aluminum oxide dispersion according to claim 1 , wherein the aluminum oxide powder in a 4 percent dispersion exhibits a pH value of 3 to 5.
4. The aluminum oxide dispersion according to claim 1 , wherein the aluminum oxide particles have a mean aggregate diameter d 50 of less than 100 nm.
5. The aluminum oxide dispersion according to claim 1 , wherein it is free from particles with a diameter of more than 1 μm.
6. The aluminum oxide dispersion according to claim 1 , wherein the aluminum oxide content is 40 to 60 wt. %.
7. The aluminum oxide dispersion according to claim 1 , wherein the pH value is 6 to 8.
8. The aluminum oxide dispersion according to claim 1 , wherein the zeta potential is less than −15 mV.
9. The aluminum oxide dispersion according to claim 8 , wherein the zeta potential is in the range of from −25 to −40 mV.
10. The aluminum oxide dispersion according to claim 1 , wherein the at least dibasic hydroxy-carboxylic acid present dissolved in the dispersion is citric acid or tartaric acid.
11. The aluminum oxide dispersion according to claim 10 , wherein the dibasic hydroxy-carboxylic acid comprises citric acid.
12. The aluminum oxide dispersion according to claim 10 , wherein the dibasic hydroxy-carboxylic acid comprises tartaric acid.
13. The aluminum oxide dispersion according to claim 1 , which has an isoelectric point at a pH of from about 9 to 10.
14. The aluminum oxide dispersion according to claim 1 , which is stable for at least six months.
15. A process for the production of the aluminum oxide dispersion according to claim 1 , comprising:
first placing in water one or several at least dibasic hydroxycarboxylic acids present dissolved in the dispersion and at least one salt of a dialkali metal hydrogen phosphate and/or alkali metal dihydrogen phosphate and in a quantity of 0.3-3×10 −6 mol/m 2 specific surface area,
adding all at once in portions or continuously the aluminum oxide particles, corresponding to the desired quantity, in the dispersion, and
dispersing by an energy input of more than 1000 kJ/m 3 .
16. The process according to claim 15 , wherein the dispersion is firstly performed with an energy input of less than 1000 kJ/m 3 with the formation of a predispersion, the predispersion is divided into at least two part streams, said part streams are placed in a high energy mill under a pressure of at least 500 bar, released via a nozzle and allowed to impinge on one another in a gas- or liquid-filled reaction chamber and the high energy grinding is optionally repeated one or several times.
17. A process comprising coating a glass, ceramic or metal surface with the aluminum oxide dispersion according to claim 1 .
18. A lacquer produced from the aluminum oxide dispersion according claim 1 .