Manufacture process
View Patent ↗The present invention relates to a new iron containing phosphate adsorbent and its use e.g. for treating hyperphosphataemia.
1. A process for preparing an iron(III)-based phosphate adsorbent comprising iron(III) oxide-hydroxide, starch and sucrose, said process comprising:
(i) reacting an aqueous solution of iron(III) salt with an aqueous base at a pH from between 6 and 10 to form a mixture in which an iron oxide hydroxide precipitate begins to form;
(ii) adding starch to the mixture of step i) prior to complete formation of the iron oxide hydroxide precipitate;
(iii) allowing complete formation of the iron oxide hydroxide precipitate to occur;
(iv) isolating the precipitate formed according to step (iii);
(v) suspending the isolated precipitate from step (iv) in an aqueous solution;
(vi) adding sucrose and optionally at least one excipient selected from a preservative and a binder; and
(vii) fluidized spray drying the solution from step to (vi) to yield an iron(III)-based phosphate adsorbent as a dry powder.
2. The process according to claim 1 , wherein at least one washing is performed between step (iv) and (v).
3. The process according to 2 , wherein in step (i) the pH of the solution is maintained at a constant value between 6 and 8.
4. The process according to claim 2 , further comprising the step (viii) of granulating the dry powder in the presence of an excipient selected from a binder and a lubricant to yield an iron(III)-based phosphate adsorbent as a granulate.
5. The process according to claim 4 , wherein the process further comprises the step (ix) of tableting the granulate in the presence of an excipient selected from the group consisting of a filler, a binder, a disintegrant, a flow agent, a lubricant, and mixtures thereof.
6. The process according to claim 1 , wherein the iron(III)-based phosphate adsorbent comprises starch in an amount of about 10% to about 35% by weight.
7. The process according to claim 6 , wherein the iron(III)-based phosphate adsorbent comprises sucrose in an amount of about 5% to about 50% by weight.
8. The process according to claim 6 , wherein the iron(III)-based phosphate adsorbent comprises iron in an amount of at least 10% by weight.
9. The process according to claim 1 , wherein the aqueous base is sodium carbonate.