Low alloy steel for oil country tubular goods having high sulfide stress cracking resistance
View Patent ↗Low alloy steel for oil country tubular goods contains, in percentage by mass, 0.20% to 0.35% C, 0.05% to 0.5% Si, 0.05% to 0.6% Mn, at most 0.025% P, at most 0.01% S, 0.005% to 0.100% Al, 0.8% to 3.0% Mo, 0.05% to 0.25% V, 0.0001% to 0.005% B, at most 0.01% N, and at most 0.01% O, the balance comprising Fe and impurities, the steel satisfying Expression (1): 12V+1−Mo≧0 (1) where the symbols of elements represent the contents of the elements in percentage by mass. In this way, the steel according to the present invention has high SSC resistance.
1. Low alloy steel for oil country tubular goods having high sulfide stress cracking resistance, comprising, in percentage by mass, 0.20% to 0.35% C, 0.05% to 0.5% Si, 0.05% to 0.6% Mn, at most 0.025% P, at most 0.01% S, 0.005% to 0.100% Al, 0.8% to 3.0% Mo, 0.05% to 0.25% V, 0.0001% to 0.005% B, at most 0.01% N, and at most 0.01% O, the balance comprising Fe and impurities, said low alloy steel satisfying Expression (1):
12V+1−Mo≧0 (1)
where the symbols of elements represent the contents of the elements in percentage by mass.
2. The low alloy steel for oil country tubular goods according to claim 1 , further comprising at most 0.6% Cr and satisfying Expression (2):
Mo−(Cr+Mn)≧0 (2)
where the symbols of elements represent the contents of the elements in percentage by mass.
3. The low alloy steel for oil country tubular goods according to claim 1 , further comprising at least one of at most 0.1% Nb, at most 0.1% Ti and at most 0.1% Zr.
4. The low alloy steel for oil country tubular goods according to claim 1 , further comprising at most 0.01% Ca.
5. The low alloy steel for oil country tubular goods according to claim 1 , further having at least 861 MPa yield strength.
6. The low alloy steel for oil country tubular goods according to claim 2 , further comprising at least one of at most 0.1% Nb, at most 0.1% Ti and at most 0.1% Zr.
7. The low alloy steel for oil country tubular goods according to claim 2 , further comprising at most 0.01% Ca.
8. The low alloy steel for oil country tubular goods according to claim 3 , further comprising at most 0.01% Ca.
9. The low alloy steel for oil country tubular goods according to claim 2 , further having at least 861 MPa yield strength.
10. The low alloy steel for oil country tubular goods according to claim 3 , further having at least 861 MPa yield strength.
11. The low alloy steel for oil country tubular goods according to claim 4 , further having at least 861 MPa yield strength.
12. The low alloy steel for oil country tubular goods according to claim 6 , further comprising at most 0.01% Ca.
13. The low alloy steel for oil country tubular goods according to claim 6 , further having at least 861 MPa yield strength.
14. The low alloy steel for oil country tubular goods according to claim 7 , further having at least 861 MPa yield strength.
15. The low alloy steel for oil country tubular goods according to claim 8 , further having at least 861 MPa yield strength.
16. The low alloy steel for oil country tubular goods according to claim 12 , further having at least 861 MPa yield strength.