Methods of recovery of pore-forming agents for mesostructured materials
View Patent ↗The invention provides methods of recovering a pore-forming agent from an inorganic material that defines a plurality of mesopores having a controlled cross sectional area to form a mesostructure having long-range crystallinity and also to methods of making one or more mesostructures that features removal, recovery, and/or reuse of the pore-forming agent. Suitable pore-forming agents include, for example, surfactants.
1. A method of recovering a pore-forming agent from a mesostructure, comprising:
(a) contacting a mesostructure having long-range crystallinity with an extraction agent under conditions of time and temperature sufficient to extract at least a portion of a pore-forming agent from said mesostructure, wherein said mesostructure comprises an inorganic material defining a plurality of mesopores having a controlled cross sectional area, and wherein said extraction agent is an acid:solvent mixture, wherein:
said acid of said acid:solvent mixture is selected from the group consisting of hydrochloric acid, nitric acid, sulphuric acid, a sulphonic acid, a carboxylic acid, a halogenated acid, and mixtures of two or more thereof, and
said solvent of said acid:solvent mixture is selected from the group consisting of an alcohol, acetone, dimethylformamide, methylpyrrolidone, a halogenated solvent, acetonitrile, and mixtures of two or more thereof;
(b) at least partially neutralizing the acid employed in said acid:solvent extraction with an acid neutralizing agent;
(c) separating said extraction agent containing at least a portion of said pore-foiming agent from said mesostructure;
(d) separating at least a portion of said pore-forming agent from said extraction agent; and
(e) reusing said pore-forming agent to form a mesostructure having long-range crystallinity.
2. The method of claim 1 , further comprising after step (c) calcinating said mesostructure to remove any quantity of said pore-forming agent remaining in said mesopores.
3. The method of claim 1 , wherein step (c) is performed at a temperature ranging from about room temperature to about the boiling point of said solvent in said acid:solvent mixture, wherein step (c) comprises reflux extraction.
4. The method of claim 1 , wherein step (d) is performed via distillation.
5. The method of claim 1 , wherein step (d) comprises one or more methods selected from the group consisting of distillation, precipitation, filtration, and chemical reaction.
6. The method of claim 1 , further comprising performing steps (c) at least twice.
7. The method of claim 1 , wherein said method of recovering a pore-forming agent is sufficient to remove in the range of from about 65 to about 100 weight percent of said pore-forming agent from said mesostructure.
8. The method of claim 1 , wherein said mesostructure having long-range crystallinity comprises a zeolite.
9. The method of claim 1 , wherein said pore-forming agent comprises a surfactant.
10. The method of claim 1 , wherein said mesostructure is prepared by exposing an inorganic material having long-range crystallinity to a pH controlled medium and said pore-forming agent.
11. The method of claim 10 , wherein said pH controlled medium has a pH in the range of from about 8 to about 14.
12. A method of recovering a pore-forming agent from a mesostructure, comprising:
(a) contacting a mesostructure having long-range crystallinity with an extraction agent under conditions of time and temperature sufficient to extract at least a portion of a pore-forming agent from said mesostructure, wherein said extraction agent comprises an acid:solvent mixture, and wherein said mesostructure comprises an inorganic material defining a plurality of mesopores having a controlled cross sectional area,
(b) at least partially neutralizing the acid employed in the acid:solvent extraction with an acid neutralizing agent,
(c) separating said extraction agent containing at least a portion of said pore-forming agent from said mesostructure;
(d) separating at least a portion of said pore-forming agent from said extraction agent; and
(e) reusing said pore-forming agent to form a mesostructure having long-range crystallinity.
13. The method of claim 12 , wherein said acid of said acid:solvent mixture is selected from the group consisting of hydrochloric acid, nitric acid, sulphuric acid, a sulphonic acid, a carboxylic acid, a halogenated acid, and mixtures of two or more thereof.
14. The method of claim 12 , wherein said solvent of said acid:solvent mixture is selected from the group consisting of an alcohol, acetone, dimethylformamide, methylpyrrolidone, a halogenated solvent, acetonitrile, and mixtures of two or more thereof.
15. The method of claim 12 , wherein step (c) is performed at a temperature ranging from about room temperature to about the boiling point of said solvent in said acid:solvent mixture.
16. The method of claim 12 , wherein step (c) comprises reflux extraction.
17. The method of claim 12 , wherein step (d) is performed via distillation.
18. The method of claim 12 , wherein said method of recovering a pore-forming agent is sufficient to remove in the range of from about 65 to about 100 weight percent of said pore-forming agent from said mesostructure.
19. The method of claim 12 , further comprising after step (c) calcinating said mesostructure to remove any quantity of said pore-forming agent remaining in said mesopores.
20. The method of claim 12 , wherein said mesostructure having long-range crystallinity comprises a zeolite.
21. The method of claim 12 , wherein said pore-forming agent comprises a surfactant.
22. The method of claim 12 , wherein said mesostructure is prepared by exposing an inorganic material having long-range crystallinity to a pH controlled medium and said pore-forming agent.
23. The method of claim 22 , wherein said pH controlled medium has a pH in the range of from about 8 to about 14.