Method of fabricating carbon fiber reinforced composite material parts
View Patent ↗A method of fabricating a composite material part having carbon fiber reinforcement densified by a matrix, including making a coherent fiber preform of carbon fibers presenting holes formed from at least a first face of the preform, and densifying the preform by depositing therein a material constituting a matrix by means of a chemical vapor infiltration type process. The holes are formed by causing a plurality of non-rotary elongate tools to penetrate simultaneously, the tools being substantially mutually parallel and presenting on their surfaces roughnesses or portions in relief suitable for breaking and/or transferring fibers they encounter, the tools being caused to penetrate simultaneously by moving a support carrying the tools, and the tools being selected to have a cross-section that makes it possible to obtain in the carbon fiber preform holes that present a cross-section with a mean dimension lying in the range 50 μm to 500 μm.
1. A method of fabricating a composite material part having carbon fiber reinforcement densified by a matrix, the method comprising the steps of:
making a coherent fiber preform of carbon fibers, the making of the fiber preform, including superposing fiber plies and bonding the fiber plies together by needling progressively as they are superposed one on another using first needles having a first working section;
forming holes in the fiber preform by simultaneous penetration of the preform by a plurality of non-rotary second barbed needles that are substantially mutually parallel and are distinct from the first needles, the simultaneous penetration of the second barbed needles being achieved by moving a support carrying the second barbed needles, the second barbed needles having a working cross-section larger than the working cross-section of the first needles to form within the carbon fiber preform holes extending from at least a first face of the carbon fiber preform and having a cross-section of a mean dimension lying in the range of 50 μm to 500 μm; and
densifying the preform by a chemical vapor infiltration type process to deposit therein a material constituting the matrix.
2. A method according to claim 1 , wherein a fiber preform is made of carbon fibers with holes having a mean density, measured over said first face, lying in the range 0.25 holes/cm 2 to 16 holes/cm 2 .
3. A method according to claim 1 , wherein a fiber preform is made of carbon fibers with an open area measured over said first face representing 0.025% to 2% of the total area of said first face.
4. A method according to claim 1 , wherein the tools are caused to penetrate over a distance corresponding to at least half the dimension of the preform measured parallel to the holes between the first face of the preform and a face opposite thereto.
5. A method according to claim 1 , in which the fiber preform of carbon fibers is made by making a coherent fiber preform out of carbon-precursor fibers and carbonizing the fiber substrate to transform the carbon precursor into carbon, wherein the holes are formed after the fiber substrate has been carbonized.
6. A method according to claim 1 , in which the fiber preform of carbon fibers is made by making a coherent fiber preform out of carbon-precursor fibers and carbonizing the fiber substrate to transform the carbon precursor into carbon, wherein the holes are formed in the fiber substrate before the fiber substrate is carbonized.
7. A method according to claim 6 , wherein the holes are formed while making the fiber substrate out of carbon-precursor fibers.
8. A method according to claim 7 , wherein the second barbed needles are mounted on the same support as the first needles.
9. A method according to claim 1 , wherein the fiber preform made of carbon fibers is made by preparing a coherent fiber substrate from carbon fibers and subsequently forming the holes.
10. A method according to claim 1 , wherein the fiber preform made of carbon fibers is made by preparing a coherent fiber substrate directly from carbon fibers, followed by a step of additional carbonization, and the holes are formed in the fiber substrate after the additional carbonization.
11. A method according to claim 1 , wherein the fiber preform made of carbon fibers is made by preparing a coherent fiber substrate directly from carbon fibers followed by a step of additional carbonization, and the holes are formed in the fiber substrate before the additional carbonization.
12. A method according to claim 1 , wherein the second barbed needles have a working cross-section that is several times greater than the section of the holes to be made.