High-yield synthesis of brookite TiO
View Patent ↗A method for forming non-agglomerated brookite TiO 2 nanoparticles without the use of expensive organic surfactants or high temperature processing. Embodiments of this invention use titanium isopropoxide as the titanium precursor and isopropanol as both the solvent and ligand for ligand-stabilized brookite-phase titania. Isopropanol molecules serve as the ligands interacting with the titania surfaces that stabilize the titania nanoparticles. The isopropanol ligands can be exchanged with other alcohols and other ligands during or after the nanoparticle formation reaction.
1. A method for forming ligand-stabilized titania nanoparticles, comprising:
adding a dilute water-in-isopropanol solution to an isopropanol solution of titanium isopropoxide to form a reaction solution, wherein the step of adding is performed at a sufficiently slow rate to avoid amorphous powder formation and micron-sized particle formation; and
mixing the reaction solution until ligand-stabilized titania nanoparticles form.
2. The method of claim 1 , further comprising stirring the isopropanol solution of titanium isopropoxide while adding the dilute water-in-isopropanol solution.
3. The method of claim 1 , wherein the dilute water-in-isopropanol solution is added dropwise.
4. The method of claim 1 , wherein the isopropanol solution of titanium isopropoxide has a volumetric ratio of isopropanol to titanium isopropoxide greater than or equal to approximately 15:1.
5. The method of claim 1 , wherein the dilute water-in-isopropanol solution has a volumetric ratio of isopropanol to water greater than or equal to approximately 100:1.
6. The method of claim 1 , wherein the isopropanol solution of titanium isopropoxide has an approximately 25:1 volumetric ratio of isopropanol to titanium isopropoxide and the dilute water-in-isopropanol solution has an approximately 400:1 volumetric ratio of isopropanol to water.
7. The method of claim 1 , wherein the step of mixing is performed for at least one hour.
8. The method of claim 1 , wherein the isopropanol solution of titanium isopropoxide further comprises a silane and triethanolamine.
9. The method of claim 8 , wherein the silane is a vinyl terminated silane.
10. The method of claim 1 , further comprising:
isolating the ligand-stabilized titania nanoparticles from the reaction solution;
suspending the ligand-stabilized titania nanoparticles in a ligand exchange solution, wherein the ligand exchange solution comprises replacement ligands for replacing ligands bound to surfaces of the ligand-stabilized titania nanoparticles;
exchanging the ligands bound to the surfaces by the replacement ligands by mixing the ligand-stabilized titania nanoparticles in the exchange solution.
11. The method of claim 10 , wherein the replacement ligands are selected from the group consisting of alcohols, carboxylic acids, phosphonic acids, amines, phosphines, phosphine oxides, and alkoxysilanes.
12. The method of claim 10 , wherein the exchange solution comprises a solution of decanol in chloroform, the suspending is by sonication, and the mixing is by stirring for greater than approximately 1 hour.