Combustion-Assisted Substrate Deposition Method For Producing Carbon Nanosubstances
The present invention provides a combustion-based method and apparatus for producing and isolating carbon nanotubes. The nanotubes are formed when hot combustion gases are contacted with a catalytic surface, which is readily separated from the catalyst support and subsequently dissolved. The process is suitable for large-scale manufacture of carbon nanotubes.
1 . A method for producing carbon nanotubes, comprising the steps of:
(a) establishing a flame with a carbon-containing fuel and an oxygen-containing gas, thereby producing a hot post-combustion gas; and
(b) contacting the hot post-combustion gas with the surface of a harvesting layer comprising a nanotube-forming catalyst thereby producing carbon nanotubes on said surface.
2 . The method of claim 1 , wherein the harvesting layer comprises a readily-soluble metal salt, oxide or hydroxide.
3 . A method for producing carbon nanotubes, comprising the steps of:
(a) providing a combustible gas mixture comprising a carbon-containing fuel and an oxygen-containing gas;
(c) establishing a flame with said combustible gas mixture, thereby producing a hot post-combustion gas; and
(d) contacting the hot post-combustion gas with the surface of a harvesting layer comprising a nanotube-forming catalyst, thereby producing carbon nanotubes on said surface.
4 . The method of claim 3 , wherein the harvesting layer comprises a readily-soluble metal salt, oxide or hydroxide.
5 . The method of claim 4 wherein the harvesting layer comprises a readily-soluble material selected from the group consisting of readily-soluble metal oxides, metal carbonates, metal sulfates, metal phosphates, and metal hydroxides.
6 . The method of claim 5 , wherein the harvesting layer comprises a readily-soluble oxide or hydroxide of silicon, zinc, an alkali metal, or an alkaline earth metal.
7 . The method of claim 6 , wherein the harvesting layer comprises magnesium oxide or lithium silicate.
8 . The method of claim 4 , wherein the harvesting layer is disposed on the surface of a solid support, wherein said harvesting layer consists essentially of a readily-soluble metal salt, oxide, or hydroxide.
9 . The method of claim 8 , wherein the harvesting layer consists essentially of a readily-soluble material selected from the group consisting of metal oxides, metal carbonates, metal sulfates, metal phosphates, and metal hydroxides.
10 . The method of claim 9 , wherein the readily-soluble material is an oxide or hydroxide of silicon, zinc, an alkali metal, or an alkaline earth metal.
11 . The method of claim 10 , wherein the readily-soluble material is magnesium oxide or lithium silicate.
12 . The method claim 3 , wherein the catalyst comprises at least one metal selected from the group consisting of Ni, Mo, Co, Cr, Fe, Ti, and V.
14 . The method of claim 12 , wherein the catalyst comprises Co and Ni.
15 . The method of any claim 4 , wherein the temperature of the post-combustion gas in contact with the solid surface is between about 480° C. and about 670° C.
16 . The method claim 3 , further comprising the step of treating the harvesting layer with a harvesting reagent so as to separate the carbon nanotubes from the harvesting layer.
17 . The method of claim 11 , wherein the readily-soluble material is magnesium oxide, and further comprising the step of treating the solid support with aqueous nitric acid so as to separate the carbon nanotubes from the support.
18 . The method of claim 11 , wherein the readily-soluble material is lithium silicate, and further comprising the step of treating the solid support with aqueous sodium hydroxide so as to separate the carbon nanotubes from the support.
19 . An apparatus for the manufacture of carbon nanotubes, comprising:
(a) a first gas inlet for introducing an oxygen-containing gas composition;
(b) a second gas inlet for introducing a gaseous carbon-containing fuel composition;
(c) a mixing chamber in communication with said first ad second inlets, for combining the oxygen-containing gas composition and the gaseous carbon-containing fuel composition so as to generate a combustible gas mixture;
(d) a burner in communication with said mixing chamber, for maintaining a flame in which the combustible gas mixture is converted into a hot post-combustion gas; and
(e) a solid support disposed on the flame side of said burner, in the region occupied by the flame and hot post-combustion gas;
wherein the surface of said solid support comprises a harvesting layer and a carbon nanotube-forming catalyst.
20 . The apparatus of claim 19 , further comprising an insulation means for at least partially isolating the hot-post combustion gas from the environment.
21 . The apparatus of claim 20 , further comprising a conveyance means for transporting the solid support into and out of the region occupied by the flame and post-combustion gas.
22 . The method of claim 2 wherein the harvesting layer comprises a readily-soluble material selected from the group consisting of readily-soluble metal oxides, metal carbonates, metal sulfates, metal phosphates, and metal hydroxides.
23 . The method of claim 22 , wherein the harvesting layer comprises a readily-soluble oxide or hydroxide of silicon, zinc, an alkali metal, or an alkaline earth metal.
24 . The method of claim 23 , wherein the harvesting layer comprises magnesium oxide or lithium silicate.
25 . The method of claim 2 , wherein the harvesting layer is disposed on the surface of a solid support, wherein said harvesting layer consists essentially of a readily-soluble metal salt, oxide, or hydroxide.
26 . The method of claim 25 , wherein the harvesting layer consists essentially of a readily-soluble material selected from the group consisting of metal oxides, metal carbonates, metal sulfates, metal phosphates, and metal hydroxides.
27 . The method of claim 26 , wherein the readily-soluble material is an oxide or hydroxide of silicon, zinc, an alkali metal, or an alkaline earth metal.
28 . The method of claim 27 , wherein the readily-soluble material is magnesium oxide or lithium silicate.
29 . The method of claim 1 , wherein the catalyst comprises at least one metal selected from the group consisting of Ni, Mo, Co, Cr, Fe, Ti, and V.
30 . The method of claim 29 , wherein the catalyst comprises Co and Ni.
31 . The method of claim 2 , wherein the temperature of the post-combustion gas in contact with the solid surface is between about 480° C. and about 670° C.
32 . The method of claim 1 , further comprising the step of treating the harvesting layer with a harvesting reagent so as to separate the carbon nanotubes from the harvesting layer.
33 . The method of claim 28 , wherein the readily-soluble material is magnesium oxide, and further comprising the step of treating the solid support with aqueous nitric acid so as to separate the carbon nanotubes from the support.
34 . The method of claim 28 , wherein the readily-soluble material is lithium silicate, and further comprising the step of treating the solid support with aqueous sodium hydroxide so as to separate the carbon nanotubes from the support.