Plasticizer Compositions For Flexible Closed Cell Foams
Foamable compositions based on rigid organic polymers such as polyvinyl chloride contain as the plasticizer a blend of a) a liquid oligomeric ester of phthalic acid, at least one aliphatic dicarboxylic acid or a mixture thereof; and b) a total of at least 15 weight percent, based on total plasticizer, of at least one ester of benzoic acid and/or an alkyl-substituted benzoic acid.
1 - 7 . (canceled)
8 . A foamable plastisol comprising a dispersion of finely divided rigid thermoplastic organic polymer and an effective amount of a plasticizer for said polymer, wherein said plasticizer comprises:
a liquid polyester comprising repeating units exhibiting at least one formula selected from the group consisting of —(O)CC 6 H 4 C(O)OR 1 O— and
—(O)CR 2 C(O)OR 1 O—, and terminal units exhibiting a formula selected from the group consisting of —OR 3 and —(O)CR 4 , wherein the weight average molecular weight of said polyester is at least 500 grams per mole; and wherein R 1 is selected from the group consisting of alkylene and oxoalkylene radicals and contains from 2 to 10 carbon atoms, R 2 is selected from the group consisting of a single bond and alkylene radicals containing from 1 to 12 carbon atoms; R 3 represents an alkyl radical containing from 1 to 24 carbon atoms, and R 4 is at least one member selected from the group consisting of the hydrogen atom and alkyl radicals containing from 1 to 30 carbon atoms; and
an effective amount of at least one ester derived from a) at least one acid selected from the group consisting of benzoic acid and alkyl-substituted benzoic acids, wherein said alkyl substituent contains from 1 to 6 carbon atoms, and b) at least one alcohol selected from the group consisting of mono- and polyhydric alcohols, wherein said alcohol contains from 1 to 12 carbon atoms.
9 . The plastisol according to claim 8 wherein
the weight average molecular weight of said polyester is from 500 to 22,000 grams per mole;
R 2 contains from 2 to 10 carbon atoms;
R 3 contains from 6 to 12 carbon atoms;
R 4 contains from 2 to 18 carbon atoms; and
said ester is a benzoic acid ester.
10 . The plastisol according to claim 9 wherein the concentration of said ester is from 15 to 70 percent, based on the total weight of said plasticizer, and wherein the hydroxyl number of said composition is less than 30.
11 . The plastisol according to claim 10 wherein the concentration of said ester is from 30 to 60 weight percent, based on the total weight of said plasticizer.
12 . The plastisol according to claim 8 wherein said terminal units are —OR 3 .
13 . The plastisol according to claim 8 wherein said rigid thermoplastic organic polymer is polyvinyl chloride.
14 . The foamable plastisol according to claim 8 , wherein the composition further comprises a blowing agent precursor.
15 . The plastisol according to claim 13 , wherein no greater than 60 weight percent of the polymer comprises an additional polymer effective for modifying the plasticizer absorption and viscosity of the foamable thermoplastic polymer composition.
16 . The plastisol according to claim 15 , wherein the polymer is polyvinyl chloride.
17 . The plastisol according to claim 12 , wherein the composition further comprises a heat stabilizer, an inert filler, a blowing agent activator, and a surfactant.