Process to increase the oleophobicity of PTFE, and resulting oleophobic articles
View Patent ↗Method of making a oleophobic layer on a fluoropolymer (e.g., polytetrafluoroethylene (PTFE)). The oleophobic layer includes a fluoroalkyl acrylate copolymer. The fluoropolymer may be an expanded PTFE formed into a porous membrane. The oleophobicity may be sufficient to repel #8 oil (n-heptane) in accordance with AATCC Test Method 118. There are also coated articles including fluoropolymers and oleophobic layers made from fluoroalkyl acrylate copolymers.
1. A method of increasing the oleophobicity of a fluoropolymer, the method comprising the steps of:
forming an aqueous oleophobic treatment composition by mixing a solvent, water, and a fluoroalkyl acrylate copolymer;
casting the aqueous oleophobic treatment composition on the fluoropolymer; and
drying and curing the aqueous oleophobic treatment composition such that the cured oleophobic treatment on the fluoropolymer can repel #8 oil according to AATCC test method 118 for oil repellancy.
2. The method of claim 1 , wherein the fluoropolymer comprises a porous membrane comprising expanded polytetrafluoroethylene membrane.
3. The method of claim 1 , wherein the solvent comprises at least one alcohol-based solvent chosen from the group consisting of isopropyl alcohol, methanol, ethanol, propanol, isobutanol, butanol, propylene glycol, and ethylene glycol.
4. The method of claim 1 , wherein the aqueous oleophobic treatment composition comprises 0.1-10 wt % fluoroalkyl acrylate copolymer.
5. The method of claim 1 , wherein the aqueous oleophobic treatment composition comprises 1-5 wt % fluoroalkyl acrylate copolymer.
6. The method of claim 1 , wherein the aqueous oleophobic treatment composition comprises 2-3 wt % fluoroalkyl acrylate copolymer.
7. The method of claim 1 , wherein the step of drying and curing comprises (i) exposure to a temperature sufficient to evaporate the solvent and/or water and (ii) exposure to a temperature to adhere the fluoroalkyl acrylate copolymer to the fluoropolymer.
8. The method of claim 1 , wherein the step of drying and curing comprises (i) exposure to a temperature between 100 and 350° C. for up to 10 minutes and (ii) exposure to a temperature between 350 and 550° C. for up to 5 minutes.
9. A method of repelling liquid contaminants from a surface of a porous membrane comprising polytetrafluoroethylene, the method comprising the steps of:
forming an aqueous oleophobic treatment composition by mixing a solvent, water, and a fluoroalkyl acrylate copolymer;
casting the aqueous oleophobic treatment composition on the porous membrane by spraying the aqueous oleophobic treatment composition and removing excess liquid from the porous membrane; and
drying and curing the aqueous oleophobic treatment composition; and
applying a liquid contaminant to the porous membrane having the cured oleophobic treatment, wherein the liquid contaminant comprises n-heptane, motor oil, diesel, or gasoline, and wherein the porous membrane exhibits oleophobicity to the liquid contaminant such that the cured oleophobic treatment on the fluoropolymer can repel #8 oil according to AATCC test method 118 for oil repellancy.
10. The method of claim 9 , wherein the aqueous oleophobic treatment composition comprises 0.1-10 wt % fluoroalkyl acrylate copolymer.
11. The method of claim 9 , wherein the aqueous oleophobic treatment composition comprises 1-5 wt % fluoroalkyl acrylate copolymer.
12. The method of claim 9 , wherein the aqueous oleophobic treatment composition comprises 2-3 wt % fluoroalkyl acrylate copolymer.